LATI Latilub 62-06GR PA6, Graphite Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer LATI
Trade Name Latilub
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latilub 62-06GR PA6, Graphite Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Self-lubricating product based on Polyamide 6 (PA6). Graphite. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.17 g/cc
0.0423 lb/in³
Linear Mold Shrinkage, Flow 0.0090 - 0.0125 cm/cm
0.0090 - 0.0125 in/in
Linear Mold Shrinkage, Transverse 0.0095 - 0.0135 cm/cm
0.0095 - 0.0135 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 75.0 MPa
10900 psi
Elongation at Break 6.0 %
6.0 %
Elongation at Yield 3.5 %
3.5 %
Tensile Modulus 4.50 GPa
653 ksi
Charpy Impact Unnotched 7.50 J/cm²
35.7 ft-lb/in²
Charpy Impact, Notched 0.300 J/cm²
1.43 ft-lb/in²
Coefficient of Friction, Dynamic 0.20
0.20
Coefficient of Friction, Static 0.24
0.24
K (wear) Factor 16.0 x 10-8 mm³/N-M
7.94 x 10-10 in³-min/ft-lb-hr
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 195 °C
383 °F
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
167 °F
Vicat Softening Point 205 °C

@Load 5.00 kg
 401 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 230 - 250 °C
446 - 482 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa