LATI Latamid 66 VH2 G/30 PA 66, 30% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer LATI
Trade Name Latamid
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LATI Latamid 66 VH2 G/30 PA 66, 30% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Polyamide 66 (PA66) based compound. Improved thermal stabilization. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
Linear Mold Shrinkage, Flow 0.0035 - 0.0065 cm/cm
0.0035 - 0.0065 in/in
Linear Mold Shrinkage, Transverse 0.0075 - 0.0105 cm/cm
0.0075 - 0.0105 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 65.0 MPa
<br>@Temperature 150 °C
 9430 psi
<br>@Temperature 302 °F
70.0 MPa
<br>@Temperature 120 °C
 10200 psi
<br>@Temperature 248 °F
80.0 MPa
<br>@Temperature 90.0 °C
 11600 psi
<br>@Temperature 194 °F
100 MPa
<br>@Temperature 60.0 °C
 14500 psi
<br>@Temperature 140 °F
150 MPa
<br>@Temperature 23.0 °C
 21800 psi
<br>@Temperature 73.4 °F
Elongation at Break 2.5 %
<br>@Temperature 23.0 °C
 2.5 %
<br>@Temperature 73.4 °F
4.5 %
<br>@Temperature 60.0 °C
 4.5 %
<br>@Temperature 140 °F
5.0 %
<br>@Temperature 90.0 °C
 5.0 %
<br>@Temperature 194 °F
5.5 %
<br>@Temperature 120 °C
 5.5 %
<br>@Temperature 248 °F
5.5 %
<br>@Temperature 150 °C
 5.5 %
<br>@Temperature 302 °F
Elongation at Yield 4.0 %
<br>@Temperature 60.0 °C
 4.0 %
<br>@Temperature 140 °F
5.0 %
<br>@Temperature 90.0 °C
 5.0 %
<br>@Temperature 194 °F
5.5 %
<br>@Temperature 120 °C
 5.5 %
<br>@Temperature 248 °F
5.5 %
<br>@Temperature 150 °C
 5.5 %
<br>@Temperature 302 °F
Tensile Modulus 3.30 GPa
<br>@Temperature 150 °C
 479 ksi
<br>@Temperature 302 °F
3.80 GPa
<br>@Temperature 120 °C
 551 ksi
<br>@Temperature 248 °F
5.00 GPa
<br>@Temperature 90.0 °C
 725 ksi
<br>@Temperature 194 °F
6.20 GPa
<br>@Temperature 60.0 °C
 899 ksi
<br>@Temperature 140 °F
10.4 GPa
<br>@Temperature 23.0 °C
 1510 ksi
<br>@Temperature 73.4 °F
Charpy Impact Unnotched 5.00 J/cm²
<br>@Temperature -20.0 °C
 23.8 ft-lb/in²
<br>@Temperature -4.00 °F
5.50 J/cm²
<br>@Temperature 23.0 °C
 26.2 ft-lb/in²
<br>@Temperature 73.4 °F
Charpy Impact, Notched 0.500 J/cm²
<br>@Temperature -20.0 °C
 2.38 ft-lb/in²
<br>@Temperature -4.00 °F
0.700 J/cm²
<br>@Temperature 23.0 °C
 3.33 ft-lb/in²
<br>@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 130 °C
266 °F
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
Deflection Temperature at 1.8 MPa (264 psi) 245 °C
473 °F
Vicat Softening Point 250 °C
<br>@Load 5.00 kg
 482 °F
<br>@Load 11.0 lb
Flammability, UL94 HB
<br>@Thickness 3.00 mm
 HB
<br>@Thickness 0.118 in
HB
<br>@Thickness 1.50 mm
 HB
<br>@Thickness 0.0591 in
HB
<br>@Thickness 0.750 mm
 HB
<br>@Thickness 0.0295 in
Oxygen Index 27 %
27 %
Processing Properties Metric English Comments
Melt Temperature 270 - 290 °C
518 - 554 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 90.0 - 100 °C
<br>@Time 10800 sec
 194 - 212 °F
<br>@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa