LATI LATISTAT 48/9900-03 Ethylene Vinyl Acetate (EVA) Base Conductive Plastic  (Unverified Data**)

Category Polymer , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate; Molded/Extruded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI LATISTAT 48/9900-03 Ethylene Vinyl Acetate (EVA) Base Conductive Plastic  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Latistat materials have low specific resistivity. They feature partial electrical conductivity. Selected functional additives give materials with low specific resistivity and reasonable mechanical properties. The LATISTAT compounds are used in all applications where product surface must be completely and permanently free of static charges. Addition of carbons supplying electric semi-conductivity will diminish the flowability and good surface finish of the materials, and limiting the prospects of obtaining colored products.Applications: cabinets, containers, boxes for storage and handling of discharge-sensitive electronic components, casings and bodies for electrical and mechanical components to be used in areas where flammable and explosive materials are processed, parts for typewriters, printers, photocopiers, parts for textile machinery, racks and tracks for printed circuits; electro-medical equipment.Specific Notes for this Material: ethylene vinyl acetate base (EVA); low specific resistivity; good flexibility and impact resistance.Disclaimer from LATI: This document contains information based on average values as obtained from the results of laboratory tests and observations made on LATI materials. Tested materials were injection molded, used in their natural color, and conditioned in compliance with Standard ASTM D 618, procedure A. These values refer to LATI's best technical and scientific knowledge at the moment of testing and cannot be used as a basis for the development of applications. For a better assessment of the materials, you are kindly requested to contact LATI's technical or commercial offices, which are at your disposal and will supply detailed information on the most suitable characteristics for their intended use. With reference to DPR n.224 dated May 24, 1988, issued in accordance with EC Guide-lines 85/374, LATI Industria Termoplastici S.p.A. declines all responsibility arising from an improper use of the products described in this document.All data provided by LATI.
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ISO 1183
Linear Mold Shrinkage 0.010 cm/cm
0.010 in/in
LATI
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
LATI
Mechanical Properties Metric English Comments
Hardness, Rockwell M 28
28
ASTM D785
Tensile Strength, Ultimate 11.0 MPa
1600 psi
ISO 527
Flexural Modulus 0.130 GPa
18.9 ksi
ASTM D790
Izod Impact, Notched NB

@Temperature -20.0 °C
NB

@Temperature -4.00 °F
ASTM D256
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ASTM D256
NB

@Temperature -40.0 °C
NB

@Temperature -40.0 °F
ASTM D256
Charpy Impact Unnotched >= 30.0 J/cm²

@Temperature -20.0 °C
>= 143 ft-lb/in²

@Temperature -4.00 °F
DIN 53453
>= 30.0 J/cm²

@Temperature -40.0 °C
>= 143 ft-lb/in²

@Temperature -40.0 °F
DIN 53453
>= 30.0 J/cm²

@Temperature 23.0 °C
>= 143 ft-lb/in²

@Temperature 73.4 °F
DIN 53453
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 42.0 °C
108 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 34.0 °C
93.2 °F
ASTM D648
Vicat Softening Point 49.0 °C
120 °F
50°C/h 50N; ISO 306
Electrical Properties Metric English Comments
Surface Resistance 1000 ohm
1000 ohm
IEC 93
Processing Properties Metric English Comments
Melt Temperature 190 - 200 °C
374 - 392 °F
Mold Temperature 20.0 - 40.0 °C
68.0 - 104 °F
Drying Temperature 70.0 - 80.0 °C
158 - 176 °F
Temperature can be reduced when using vacuum ovens.
Dry Time >= 3 hour
>= 3 hour
Drying time can be reduced when using vacuum ovens.
Descriptive Properties Value Comments
Injection Speed medium