Ineos K44-15-186 Polyethylene Copolymer

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Extruded
Manufacturer	Ineos Olefins & Polymers USA
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ineos K44-15-186 Polyethylene Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

K44-15-186 is a blue high-density polyethylene copolymer designed specifically for extrusion of pipe by blending K44-15-122 natural resin with G38-70C BLU II concentrate or an approved equivalent. It has NSF Standard 14 certification and compiles with ANSI/NSF Standard 61 health effects requirements and is recognized by the Plastic Pipe Institute as having a PE 3608 (formerly PE 3408) rating.Information provided by Ineos Olefins & Polymers USA

Physical Properties	Metric	English	Comments
Density	0.944 g/cc	0.0341 lb/inÂ³	Natural; ASTM D4883
Environmental Stress Crack Resistance	>= 2000 hour	>= 2000 hour	Condition B, 10%; ASTM D1693
	>= 5000 hour	>= 5000 hour	Condition C; ASTM D1693
Melt Flow	12.5 g/10 min @Load 21.6 kg, Temperature 190 Â°C	12.5 g/10 min @Load 47.6 lb, Temperature 374 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
PENT	>= 30 hour	>= 30 hour	ASTM F147
Hardness, Shore D	68	68	ASTM D2240
Tensile Strength at Break	31.0 MPa	4500 psi	2 in/min; ASTM D638
Tensile Strength, Yield	22.8 MPa	3300 psi	2 in/min; ASTM D638
Elongation at Break	>= 800 %	>= 800 %	2 in/min; ASTM D638
2% Secant Modulus	0.827 GPa	120 ksi	ASTM D790
Izod Impact, Notched	3.20 J/cm	6.00 ft-lb/in	ASTM D256
Hydrostatic Design Basis	11.0 MPa @Temperature 23.0 Â°C	1600 psi @Temperature 73.4 Â°F	ASTM D2837

Thermal Properties	Metric	English	Comments
Vicat Softening Point	126 Â°C	259 Â°F	ASTM D1525
Brittleness Temperature	<= -118 Â°C	<= -180 Â°F	ASTM D746

Descriptive Properties	Value	Comments
Cell Classification	345464E	ASTM D3350