Huntsman Rexell® V8401 Cast Film Extrusion LLDPE (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman Rexell® V8401 Cast Film Extrusion LLDPE
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultra linear-low density copolymer, blown film extrusion, FDA compliant.Features: Excellent combination of flexibility, flex crack resistance, and low temperature properties. It also exhibits excellent sealing properties, good hot tack, and low sealing temperature.Applications: Sealing and abuse layer in coextruded multi-layer films, films with high filler content, and impact modifier in polyolefin blends.Film properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.902 g/cc | 0.0326 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 700 % | 700 % | ASTM D882 |
| Film Elongation at Break, TD | >= 700 % | >= 700 % | ASTM D882 |
| Secant Modulus, MD | 0.0760 GPa | 11.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.0970 GPa | 14.1 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 510 g | 510 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 850 g | 850 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 20.1 g/micron | 510 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 33.5 g/micron | 850 g/mil | ASTM D1922 |
| Dart Drop | 17.3 g/micron | 440 g/mil | ASTM D1709 |
| Dart Drop Test | 440 g | 0.970 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 23.0 MPa | 3340 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | >= 12.0 MPa | >= 1740 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 4.0 % | 4.0 % | ASTM D1003 |
| Gloss | 82 % | 82 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 165 - 205 °C | 329 - 401 °F |
Users viewing this material also viewed the following:
- Quadrant EPP TIVAR® Oil Filled PE-UHMW + oil (ISO Data)
- Manifattura Cattaneo PET Polyethylene Terephthalate
- Lanxess Durethan® ECO BV 30 H2 900500 Nylon 6, 30% Glass Fiber
- A. Schulman SCHULAMID® 6 GF15H 15% Glass Fiber Reinforced, Heat Impact Nylon 6
- Unitika A3130 PA6, 35% Mineral Reinforced, Conditioned
- Westlake EC4041AA Low Density Polyethylene
- DSM Stanyl® TW300 Nylon 46 (European and Asian Grade) (Cond)
- DuPont Teijin Films Melinex® 453 Polyester Film, 92 Gauge
- 3M 12034 Black 1/4" (6.4 mm) Polyurethane Foam
- Ametek P409L P/M Stainless Steel, Sintered from 6.00 g/cc Green Density
Copyright © lookpolymers.com All Rights Reserved