Lanxess Durethan® ECO BV 30 H2 900500 Nylon 6, 30% Glass Fiber
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® ECO BV 30 H2 900500 Nylon 6, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, 30% glass fibers, injection molding, heat-ageing stabilized, contains 30% pre-consumer recycled materialInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ISO 1183 |
| Bulk Density | 0.700 g/cc | 0.0253 lb/in³ | ISO 60 |
| Moisture Absorption at Equilibrium | 2.1 % | 2.1 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 7.0 % | 7.0 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.00050 - 0.0030 cm/cm | 0.00050 - 0.0030 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 | |
| Linear Mold Shrinkage, Transverse | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4 |
| 0.0060 - 0.010 cm/cm | 0.0060 - 0.010 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 145 MPa | 21000 psi | d.a.m.; ISO 527-1, -2; 5 mm/min |
| Elongation at Break | 3.0 % | 3.0 % | d.a.m.; ISO 527-1, -2; 5 mm/min |
| Tensile Modulus | 9.40 GPa | 1360 ksi | d.a.m.; ISO 527-1, -2; 1 mm/min |
| Flexural Strength | 235 MPa @Strain 3.60 % |
34100 psi @Strain 3.60 % |
d.a.m., 2 mm/min; ISO 178-A |
| Flexural Yield Strength | 230 MPa @Strain 3.50 % |
33400 psi @Strain 3.50 % |
d.a.m., 2 mm/min; ISO 178-A |
| Flexural Modulus | 8.90 GPa | 1290 ksi | d.a.m., 2 mm/min; ISO 178-A |
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 180-1A |
| <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 180-1U |
| 55.0 kJ/m² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 180-1U | |
| Charpy Impact Unnotched | 5.50 J/cm² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 179-1eU |
| 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 179-1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
d.a.m.; ISO 179-1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
d.a.m.; ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1, -3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | ISO 75-1, -2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| 280 °C | 536 °F | for test specimens; ISO 294 | |
| Mold Temperature | 80.0 °C | 176 °F | for test specimens; ISO 294 |
| 80.0 - 120 °C | 176 - 248 °F | ||
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.030 - 0.12 % | 0.030 - 0.12 % | residual; Karl Fischer Test |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 1874-PA 6, GHR, 14-090, GF30 |