Huntsman PE1205 EVA Film Extrusion  (discontinued **)

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Huntsman PE1205 EVA Film Extrusion  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
2% Vinyl Acetate EVA copolymer and FDA compliantFeatures: High clarity film with good stiffness and low temperature toughness.Applications: Film extrusion: food packaging, general purpose packaging that requires low temperature toughness.FDA Notes: Conforms to FDA regulation 21 CFR 177.1350 under condition of use C through G described in Table 2 of 21 CFR 176.170Film properties based on 1.0 guage (25 µm) thickness; blow-up ratio 2:1.Information provided by Huntsman Corporation
Physical Properties Metric English Comments
Density 0.927 g/cc
0.0335 lb/in³
ASTM D1505
Thickness 25.4 microns
1.00 mil
Melt Flow 2.0 g/10 min
2.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 48
48
ASTM D2240
Tensile Strength, Ultimate 14.0 MPa
2030 psi
ASTM D638
Tensile Strength, Yield 10.0 MPa
1450 psi
ASTM D638
Film Elongation at Break, MD 470 %
470 %
ASTM D882
Film Elongation at Break, TD 680 %
680 %
ASTM D882
Elongation at Break 560 %
560 %
ASTM D638
Modulus of Elasticity 0.338 GPa
49.0 ksi
Secant; ASTM D638
Secant Modulus, MD 0.163 GPa
23.6 ksi
ASTM D882
Secant Modulus, TD 0.190 GPa
27.6 ksi
ASTM D882
Dart Drop 4.53 g/micron
115 g/mil
ASTM D1709
Dart Drop Test 115 g
0.254 lb
ASTM D1709
Film Tensile Strength at Break, MD 23.0 MPa
3340 psi
ASTM D882
Film Tensile Strength at Break, TD 19.0 MPa
2760 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 95.0 °C
203 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 4.5 %
4.5 %
ASTM D1003
Gloss 73 %
73 %
at 45°; ASTM D523
Processing Properties Metric English Comments
Melt Temperature 182 - 193 °C
360 - 379 °F