Fujipoly Industries Sarcon® NR-c Gap Filler Pad Non-Silicone

Category Polymer
Manufacturer Fujipoly Industries
Trade Name Sarcon®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Fujipoly Industries Sarcon® NR-c Gap Filler Pad Non-Silicone.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Sarcon NR-c consists of an Acrylate resin and some thermal conductive fillers. It is a highly conformable/ thermally conductive material in a versatile sheet form that makes reliable and complete physical contact. Not electrically conductiveInformation provided by Fujipoly Industries
Physical Properties Metric English Comments
Specific Gravity 2.10 g/cc
2.10 g/cc
JIS-K-6220; ASTM D-792
2.10 g/cc
2.10 g/cc
-40°C for 1,000 hrs; JIS-K-6220; ASTM D 792
2.10 g/cc
2.10 g/cc
-40°C for 30 min and 125°C for 30 min. for 1,000 times; JIS-K-6220; ASTM D 792
2.10 g/cc
2.10 g/cc
85°C for 1,000 hrs with 85% RH; JIS-K-6220; ASTM D 792
2.10 g/cc
2.10 g/cc
80°C for 1,000 hrs; JIS-K-6220; ASTM D 792
2.20 g/cc
2.20 g/cc
125°C for 1,000 hrs; JIS-K-6220; ASTM D 792
Mechanical Properties Metric English Comments
Hardness, Shore C 28
28
85°C for 1,000 hrs with 85% RH; SRIS0101S
30.0
30.0
-40°C for 1,000 hrs; SRIS0101S
30
30
80°C for 1,000 hrs; SRIS0101S
37.0
37.0
-40°C for 30 min and 125°C for 30 min. for 1,000 times; SRIS0101S
55
55
125°C for 1,000 hrs; SRIS0101S
Hardness, Shore OO 53
53
ASTM D-2240
Tensile Strength, Yield 0.200 MPa
29.0 psi
85°C for 1,000 hrs with 85% RH; JIS-K-6251(#2); ASTM D412
0.200 MPa
29.0 psi
-40°C for 1,000 hrs; JIS-K-6251(#2); ASTM D412
0.200 MPa
29.0 psi
JIS-K-6251(#2)/ASTM D-412
0.300 MPa
43.5 psi
80°C for 1,000 hrs; JIS-K-6251(#2); ASTM D412
0.800 MPa
116 psi
125°C for 1,000 hrs; JIS-K-6251(#2); ASTM D412
0.800 MPa
116 psi
-40°C for 30 min and 125°C for 30 min. for 1,000 times; JIS-K-6251(#2); ASTM D412
Elongation at Yield 20 %
20 %
125°C for 1,000 hrs; JIS-K-6251(#2); ASTM D412
25.0 %
25.0 %
-40°C for 30 min and 125°C for 30 min. for 1,000 times; JIS-K-6251(#2); ASTM D412
150 %
150 %
JIS-K-6251(#2)/ASTM D-412
180 %
180 %
80°C for 1,000 hrs; JIS-K-6251(#2); ASTM D412
180 %
180 %
85°C for 1,000 hrs with 85% RH; JIS-K-6251(#2); ASTM D412
180 %
180 %
-40°C for 1,000 hrs; JIS-K-6251(#2); ASTM D412
Tear Strength 1.50 kN/m
8.56 pli
JIS-K-6252 (Angle)/ASTM D-624
1.70 kN/m
9.70 pli
-40°C for 1,000 hrs; JIS-K-6252(Angle); ASTM D624
1.80 kN/m
10.3 pli
80°C for 1,000 hrs; JIS-K-6252(Angle)/ASTM D 624
2.00 kN/m
11.4 pli
85°C for 1,000 hrs with 85% RH; JIS-K-6252(Angle); ASTM D 624
5.70 kN/m
32.5 pli
-40°C for 30 min and 125°C for 30 min. for 1,000 times; JIS-K-6252(Angle); ASTM D 624
7.40 kN/m
42.2 pli
125°C for 1,000 hrs; JIS-K-6252 (Angle); ASTM D 624
Thermal Properties Metric English Comments
Thermal Conductivity 1.50 W/m-K
10.4 BTU-in/hr-ft²-°F
JIS-R-2618; ASTM D2326
Maximum Service Temperature, Air 105 °C
221 °F
Minimum Service Temperature, Air -40.0 °C
-40.0 °F
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 7.00e+6 ohm-cm
7.00e+6 ohm-cm
-40°C for 1,000 hrs; JIS-K-6249; ASTM D257
2.00e+11 ohm-cm
2.00e+11 ohm-cm
JIS-K-6249/ASTM D257
8.00e+11 ohm-cm
8.00e+11 ohm-cm
85°C for 1,000 hrs with 85% RH; JIS-K 6249; ASTM D257
1.00e+12 ohm-cm
1.00e+12 ohm-cm
-40°C for 30 min and 125°C for 30 min. for 1,000 times; JIS-K-6249; ASTM D149
2.00e+12 ohm-cm
2.00e+12 ohm-cm
80°C for 1,000 hrs; JIS-K-6249; ASTM D 257
3.00e+13 ohm-cm
3.00e+13 ohm-cm
125°C for 1,000 hrs; JIS-K-6249; ASTM D257
Dielectric Strength 9.00 kV/mm
229 kV/in
-40°C for 1,000 hrs; JIS-K-6249; ASTM D149
11.0 kV/mm
279 kV/in
JIS-K-6249; ASTM D-149
18.0 kV/mm
457 kV/in
80°C for 1,000 hrs; JIS-K-6249; ASTM D 149
26.0 kV/mm
660 kV/in
125°C for 1,000 hrs; JIS-K-6249; ASTM D 149
27.0 kV/mm
686 kV/in
-40°C for 30 min and 125°C for 30 min. for 1,000 times; JIS-K-6249; ASTM D 149
Descriptive Properties Value Comments
Color Grey