ExxonMobil LLDPE LL 3001.32 Cast Linear Low Density Polyethylene Resin
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LLDPE |
| Manufacturer | Exxon Chemical |
| Trade Name | LLDPE |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil LLDPE LL 3001.32 Cast Linear Low Density Polyethylene Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: LL 3001.32 is a hexane copolymer LLDPE designed for the blown or cast film process. Films made from LL 3001.32 have outstanding tensile and toughness properties. The superior strength properties, along with excellent drawability, make this a very versatile packaging film resin.Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: NoProcessing Aid: No Thermal Stabilizer: YesApplications: Freezer FilmHeavy Duty BagsIce BagsTrash BagsInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ExxonMobil method |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 8.27 MPa | 1200 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 7.58 MPa | 1100 psi | ASTM D882 |
| Film Elongation at Break, MD | 340 % | 340 % | ASTM D882 |
| Film Elongation at Break, TD | 790 % | 790 % | ASTM D882 |
| Puncture Energy | 3.28 J | 2.42 ft-lb | ExxonMobil Method |
| Elmendorf Tear Strength MD | 300 g | 300 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 750 g | 750 g | ASTM D1922 |
| Dart Drop Test | 80.0 g | 0.176 lb | ASTM D1709A |
| Film Tensile Strength at Break, MD | 66.2 MPa | 9600 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 37.9 MPa | 5500 psi | ASTM D882 |
| 1% Secant Modulus, MD | 117 MPa | 17000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 145 MPa | 21000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | <= 255 °C | <= 491 °F | Peak Melting Point; ExxonMobil method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.2 % | 2.2 % | ASTM D1003 |
| Gloss | 89 % | 89 % | 45°; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Puncture Force | 9 lbf | ExxonMobil Method |