ExxonMobil LD 051.LQ Shrink Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer Exxon Chemical
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LD 051.LQ Shrink Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
L Product Description: LD 051.LQ blown film resin is a fractional melt index grade designed for demanding heavy duty film applications, and combines excellent strength properties with outstanding processability. Availability: Latin America, North America and South America Additive: Antiblock: 4000 ppmSlip: NoThermal Stabilizer: NoApplications:Agricultural FilmBlend PartnerCollation ShrinkConstruction FilmHeavy Duty BagsPallet Shrink FilmZipper Bag Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.919 g/cc
0.0332 lb/in³
ExxonMobil Method
Thickness 50.8 microns
2.00 mil
Melt Flow 0.25 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.25 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Antiblock Level 4000 ppm
4000 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 11.0 MPa
1600 psi
ASTM D882
Film Tensile Strength at Yield, TD 10.3 MPa
1500 psi
ASTM D882
Film Elongation at Break, MD 130 %
130 %
ASTM D882
Film Elongation at Break, TD 570 %
570 %
ASTM D882
Elmendorf Tear Strength MD 280 g
280 g
ASTM D1922
Elmendorf Tear Strength TD 120 g
120 g
ASTM D1922
Dart Drop Test 190 g
0.419 lb
ASTM D1709
Film Tensile Strength at Break, MD 25.5 MPa
3700 psi
ASTM D882
Film Tensile Strength at Break, TD 24.1 MPa
3500 psi
ASTM D882
1% Secant Modulus, MD 186 MPa
27000 psi
ASTM D882
1% Secant Modulus, TD 241 MPa
35000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 109 °C
229 °F
Peak Melting Temperature; ExxonMobil Method
Optical Properties Metric English Comments
Haze 20 %
20 %
ASTM D1003
Gloss 33 %
33 %
45°; ASTM D2457