NYC YT3WBQ Y2O3 CIP (Cold Isostatic Pressing) Granules

Category	Ceramic , Oxide
Manufacturer	Nippon Yttrium Company (NYC)
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	NYC YT3WBQ Y2O3 CIP (Cold Isostatic Pressing) Granules.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

99.9% and better high purity granules produce high quality finished ceramics. Uses include semiconductors / LCD industries, metallurgy, magnets, and electroceramics.Acrylic binder systemExcellent green propertiesEasy sintering with stable, low shrinkage rates

Physical Properties	Metric	English	Comments
Bulk Density	1.30 g/cc	0.0470 lb/in³	Apparent Density of Granules
	1.40 g/cc	0.0506 lb/in³	Tap Density of Granules
Porosity	<= 2.0 %	<= 2.0 %	after sintering at 1650°C for 2 hours in air
Particle Size	0.50 µm	0.50 µm	Raw Material; Average; D<sub>50</sub>; Microtrac HRA
	40 µm	40 µm	Granules; Average; D<sub>50</sub>; Microtrac HRA
Specific Surface Area	6.0 m²/g	6.0 m²/g	Raw material; BET

Thermal Properties	Metric	English	Comments
Shrinkage	20.0 % @Temperature 1650 °C, Time 7200 sec	20.0 % @Temperature 3000 °F, Time 2.00 hour

Component Elements Properties	Metric	English	Comments
Fe2O3	<= 0.0010 %	<= 0.0010 %	ICP-AES
Na2O	<= 0.0010 %	<= 0.0010 %	AA
Y2O3	>= 99.9 %	>= 99.9 %	TREO