ExxonMobil Exceed™ 1327KD Metallocene Polyethylene Resin (European Grade)

Category Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer Exxon Chemical
Trade Name Exceed™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Exceed™ 1327KD Metallocene Polyethylene Resin (European Grade).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Exceed 1327KD is a metallocene ethylene-hexene copolymer. It produces films which have high modulus whilst retaining good toughness. Additionally, Exceed 1327KD is fully formulated with slip and antiblock, giving a versatile ready-to-use polymer for applications such as form fill and seal.Availability: Africa & Middle East, Asia Pacific and EuropeAdditive:Antiblock: 750 ppmSlip: 1300 ppm Processing Aid: Yes Thermal Stabilizer: Yes Applications: Bag in a BoxBarrier Food Packaging Blown Film Bread Bags Food packagingForm Fill and Seal PackagingGeneral Packaging Industrial Packaging Multilayer Packaging Film Overwrap FilmPackaging FilmsPremium Trash Bags Shrink FilmStand Up PouchesTrash Bags Zipper BagInformation provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.927 g/cc
0.0335 lb/in³
ExxonMobil method
Melt Flow 1.3 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.3 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Antiblock Level 750 ppm
750 ppm
Slip Level 1300 ppm
1300 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 12.4 MPa
1800 psi
ASTM D882
Film Tensile Strength at Yield, TD 13.8 MPa
2000 psi
ASTM D882
Film Elongation at Break, MD 570 %
570 %
ASTM D882
Film Elongation at Break, TD 690 %
690 %
ASTM D882
Elmendorf Tear Strength MD 180 g
180 g
ASTM D1922
Elmendorf Tear Strength TD 500 g
500 g
ASTM D1922
Dart Drop Test 140 g
0.309 lb
ASTM D1709
Film Tensile Strength at Break, MD 51.7 MPa
7500 psi
ASTM D882
Film Tensile Strength at Break, TD 44.1 MPa
6400 psi
ASTM D882
1% Secant Modulus, MD 290 MPa
42000 psi
ASTM D882
1% Secant Modulus, TD 317 MPa
46000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point <= 253 °C
<= 487 °F
Peak Melting Point; ExxonMobil method
Optical Properties Metric English Comments
Haze 24 %
24 %
ASTM D1003
Gloss 33 %
33 %
45°; ASTM D2457