Polymer Property : Film Tensile Strength at Break, MD = 51.7 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, MD	51.7 - 75.8 MPa	7500 - 11000 psi	ASTM D882
Honeywell ACLAR® 22A (2.00 mil) Copolymer Film (discontinued **) Description: ACLAR® 22A is a copolymer film consisting primarily of chlorotrifluoroethylene (CTFE). It is a flexible transparent film used to package moisture sensitive products.Information provide..
Film Tensile Strength at Break, MD	51.7 - 75.8 MPa	7500 - 11000 psi	ASTM D882
Honeywell ACLAR® 22A (1.50 mil) Copolymer Film (discontinued **) Description: ACLAR® 22A is a copolymer film consisting primarily of chlorotrifluoroethylene (CTFE). It is a flexible transparent film used to package moisture sensitive products.Information provide..
Film Tensile Strength at Break, MD	>= 51.7 MPa	>= 7500 psi	ASTM D 882 A
Total 6410 HDPE Film Resin Unique combination of high stiffness and clarity; Good moisture barrier properties; Good processability; Good compatibility with LDPE and LLDPEApplications: paper overwrap, cup overwrap, plate overw..
Film Tensile Strength at Break, MD	51.7 MPa	7500 psi	ASTM D882, A 20 in/min
Total HDPE 6420 High Density Polyethylene, Film Resin Polyethylene: Medium molecular weight, high density film resinCharacteristics:Excellent moisture barrier propertiesLow gelsLow taste and odorHigh stiffnessGood processabilityGood compatibility with..
Film Tensile Strength at Break, MD	51.7 MPa	7500 psi	ASTM D882
Formosa Plastics Formolene® E922 Film HDPE High Density Polyethylene Medium Molecular Weight Bi-Modal Resin Designed for Film Applications Formolene® E922 is a medium molecular weight grade of HDPE designed for good processing characteristi..
Film Tensile Strength at Break, MD	51.7 MPa	7500 psi	ASTM D882
ExxonMobil Exceed™ 1327KD Metallocene Polyethylene Resin (European Grade) Product Description: Exceed 1327KD is a metallocene ethylene-hexene copolymer. It produces films which have high modulus whilst retaining good toughness. Additionally, Exceed 1327KD is fully formula..
Film Tensile Strength at Break, MD	51.7 MPa	7500 psi	ASTM D882
Dow FLEXOMER™ ETS-9064 NT 7, 0.8 mil Very Low Density Polyethylene (VLDPE) Resin FLEXOMER™ ETS-9064 NT 7 is intended for use in single of multi-layer blown-film constructions or thick sheets. Films extruded from ETS-9064 NT 7 have a high tear strength, high impact strength, an..
Film Tensile Strength at Break, MD	51.7 MPa	7500 psi	ASTM D882
Dow FLEXOMER™ ETS-9064 NT 7, 2mil Very Low Density Polyethylene (VLDPE) Resin FLEXOMER™ ETS-9064 NT 7 is intended for use in single of multi-layer blown-film constructions or thick sheets. Films extruded from ETS-9064 NT 7 have a high tear strength, high impact strength, an..
Film Tensile Strength at Break, MD	51.7 MPa	7500 psi	ASTM D882
Rogers Corporation 3001 Thermoplastic Chloro-Fluorocopolymer Bonding Film Rogers 3001 bonding film is a thermoplastic chloro-fluorocopolymer. It is recommended for bonding low dielectric constant PTFE (Teflon® fluorocarbon polymer) microwave stripline packages and other..