Eastman Eastalloy DA111 PC+PET Copolyester/Polycarbonate (discontinued **)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eastman Eastalloy DA111 PC+PET Copolyester/Polycarbonate
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ISO data as provided by the manufacturer, Eastman Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 5.3 % | 5.3 % | |
| Tensile Modulus | 1.82 GPa | 264 ksi | 1mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 6.30 J/cm² | 30.0 ft-lb/in² | Partial Break |
| 2.08 J/cm² @Temperature -30.0 °C |
9.90 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 74.0 µm/m-°C @Temperature 20.0 °C |
41.1 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | 51.0 µm/m-°C @Temperature 20.0 °C |
28.3 µin/in-°F @Temperature 68.0 °F |
|
| Specific Heat Capacity | 1.51 J/g-°C | 0.361 BTU/lb-°F | |
| Melting Point | 280 °C | 536 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | |
| Vicat Softening Point | 108 °C | 226 °F | |
| Glass Transition Temp, Tg | 112 °C | 234 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
||
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 295 - 330 °C | 563 - 626 °F |
Users viewing this material also viewed the following:
- MV Labs CA400 CaCl2·xH2O Calcium chloride hydrate
- Polimeros Mexicanos Rotolene® Black Plus Ultra Polyethylene
- Lucent Polymers GPP-210 Polypropylene, 10% Glass Fiber Reinforced, Chemically Coupled, Impact Modified
- Henkel Hysol EA 9696 Film Adhesive
- SABIC Innovative Plastics LNP LUBRICOMP DL004 PC
- Sibur BSK-1500 Styrene-Butadiene Rubber (SBR)
- ExxonMobil Diol 13 RD 40
- 3M 5640 Silicone Rubber Termination Kits
- Ravago Manufacturing Americas Hylon® N2200 HL Nylon 6/6 (discontinued **)
- Sinotek Materials Graphite Sealing Strip Fireproofing Sealing Products
Copyright © lookpolymers.com All Rights Reserved