E-Polymers TEKAMID® TB120CR Fast Crystallinity PA6 Resin

Category	Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer	E-Polymers Co. Ltd.
Trade Name	TEKAMID®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	E-Polymers TEKAMID® TB120CR Fast Crystallinity PA6 Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Polyamide (Nylon) Resin. TEKAMID is widely being used in manufacturing of automotive and industrial parts with its outstanding mechanical, thermal and chemical properties.T-series: Impact modified, Super tough productsInformation Provided by E-Polymers Co., Ltd.

Physical Properties	Metric	English	Comments
Specific Gravity	1.14 g/cc	1.14 g/cc	ASTM D792
Water Absorption	1.7 % @Time 86400 sec	1.7 % @Time 24.0 hour
Linear Mold Shrinkage	0.014 cm/cm	0.014 in/in

Mechanical Properties	Metric	English	Comments
Tensile Strength	75.5 MPa	11000 psi	ASTM D638
Elongation at Break	60 %	60 %	ASTM D638
Flexural Strength	108 MPa	15700 psi	ASTM D790
Flexural Modulus	2.65 GPa	384 ksi	ASTM D790
Izod Impact, Notched	0.441 J/cm	0.827 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	ASTM D2133
Deflection Temperature at 0.46 MPa (66 psi)	175 °C	347 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	85.0 °C	185 °F	ASTM D648
Flammability, UL94	HB	HB

Processing Properties	Metric	English	Comments
Melt Temperature	230 - 250 °C	446 - 482 °F
Mold Temperature	40.0 - 60.0 °C	104 - 140 °F

Users viewing this material also viewed the following: