- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 347 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 347 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D648 |
| Nylene® 204 (HS) , Fast Cycle Nylon 6 Description: Nylene® 204 (HS) is a fast cycle, medium viscosity, nucleated nylon 6. 204 is UL approved and automotive approved. Information provided by Custom Resins.ALM, Nylene Canada, and Custom .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D648 |
| Nylene® 454 Nylon 6, 50% RH Injection molding grade. Nylene 454 is the heat stabilized version of 451 recommended for molding applications requiring both maximum durability and toughness. Exceptional fatigue and wear resistanc.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D648 |
| Nylene® 601 Nylon 6, Extrusion Grade Dry as molded. Extrusion grade. Nylene 601 is the heat stabilized version of 600 which is a general purpose, medium viscosity, extrusion grade resin used in applications such as rods, slabs, and t.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | |
| LATI Latamid SP1 PA 6.10 Polyamide 6.10 (PA6.10). Unfilled. Low moisture absorption.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | |
| LATI Latigray 75/4-01 CX/45 PBT Radiopaque compound based on Polybutylene Terephthalate (PBT). Special mineral filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by L.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C @Thickness 3.20 mm |
347 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP KCL34A Acetal Homopolymer LNP* LUBRICOMP* KCL34A is a compound based on Acetal Homopolymer resin containing 15% PTFE, 20% Carbon Fiber. Added features of this material include: Wear Resistant, Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP LUBRICOMP KCL34A Acetal Homopolymer (Asia Pacific) LNP* Lubricomp* KCL34A is a compound based on Acetal Homopolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C @Thickness 3.20 mm |
347 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP SX93441D PA12 LNP* Lubricomp* SX93441D is a compound based on Nylon 12 containing Proprietary Fillers. Characteristics of this grade are: Internally Lubricated. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D 648 |
| Shakespeare Isocorâ„¢ SVP6105 medium viscosity PA-610 Isocorâ„¢ 6105 is a medium viscosity PA-610. This resin is specifically suited for applications requiring low moisture absorption and greater dimensional stability. Isocorâ„¢ 6105 is also .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics Valox® VX3101N PBT (Europe-Africa-Middle East) VALOX VX3101N is an unreinforced PBT injection moulding resin, with excellent flow properties, good hydrolitical stability and chemical resistance. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP GX05482 PSU LNP* THERMOCOMP* GX05482 is a compound based on Polysulfone resin containing 30% Glass Fiber. Added features of this material include: Flame Retardant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | Unannealed; ASTM D648 |
| Techmer ES Plastiblend® PA6/10 BK Nylon 610 Availability: North AmericaForms: PelletsAppearance: BlackInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics NORYL GTX GTX944 PPE+PA NORYL GTX944 is an unfilled GTX grade with improved processability and increased impact performance. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics NORYL GTX GTX944 PPE+PA (Asia Pacific) NORYL GTX944 is an unfilled GTX grade with improved processability and increased impact performance. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics NORYL GTX GTX974 PPE+PA (Europe-Africa-Middle East) NORYL GTX974 is a material especially designed for in- or on-line painted bodypanels and fenders in particular. This material combines impact performance with conductivity for electro-static paintin.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics Noryl GTX GTX976 PPE+PA (Europe-Africa-Middle East) NORYL GTX976 is a material especially designed for electrostatic painting and powder coating applications. This material combines high impact performance with conductivity in an unique way.This data.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D648 |
| A. Schulman POLYFLAM™ RPP 1133 Flame Retardant, Copolymer Polypropylene DescriptionPolyflam® RPP 1133 is a 30% glass filled, flame retardant copolymer polypropylene compound. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ISO 75 |
| Ter Hell Plastic Terez® PA/PP 7500 GF 7/1 Polyamide/Polypropylene Medium viscosity special compound with increased rigidity and low moisture absorption.Application: For molding parts with high mechanical requirements at low moisture absorption.Information provide.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D648 |
| A. Schulman POLYFLAM™ RPP 1133 Flame Retardant, Copolymer Polypropylene DescriptionPolyflam® RPP 1133 is a 30% glass filled, flame retardant copolymer polypropylene compound. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | Absolute Drying; ASTM-D648 |
| Toyobo GLAMIDE® T-802 Nylon-6 GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing a.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D648 |
| A. Schulman POLYFLAM™ RPP 1133 Flame Retardant, Copolymer Polypropylene DescriptionPolyflam® RPP 1133 is a 30% glass filled, flame retardant copolymer polypropylene compound. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | dry; ISO 75-1/-2 |
| DSM Novamid® 1011CH5KR PA6 Heat Stabilized, Easy Molding Grade |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | |
| Arkema Group Rilsan® ASR 30 Nylon 12, 30% Carbon Fiber Filled (Conditioned) Designation ISO 1874-PA12,M,16-120,CF30Rigid grade with carbon fiber filler (30%) for injection molding. Available color: black.Very high rigidity. High strength-to-weight ratio. Very low shrinkage:.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | |
| Arkema Group Rilsan® AZM 30 NOIR T6LD Nylon 12, 30% Glass Fiber Filled (Conditioned) Designation ISO 1874-PA12,MHLR,16-060,GF30Rigid grade with glass fiber (30%) for injection molding. Available color: black. Reinforced light and heat stabilizing agent. Mold-release agent.High rigid.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D648 |
| Cast Nylons Nycast® 12 Cast Nylon 12 NYCAST® 12 is specially formulated and designed to offer very low moisture absorption, superior wear resistance, dimensional stability, exceptional lubrication ability, outstanding mechanical chara.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | ASTM D648 |
| A. Schulman POLYFLAM™ RPP 1133 Flame Retardant, Copolymer Polypropylene DescriptionPolyflam® RPP 1133 is a 30% glass filled, flame retardant copolymer polypropylene compound. Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C @Thickness 6.35 mm |
347 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| PolyOne Stat-Tech™ NJ-20CF/000 Black Polyamide 12 (Nylon 12) Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compound.. |
|||