Unitika EX-1222 PA6, Dry

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer	Unitika
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Unitika EX-1222 PA6, Dry.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

High-impact nylonInformation provided by Unitika Ltd.

Physical Properties	Metric	English	Comments
Density	1.07 g/cc	0.0387 lb/in³	ISO 1183
Water Absorption	1.5 % @Time 86400 sec	1.5 % @Time 24.0 hour	ISO 62
Moisture Absorption at Equilibrium	2.2 %	2.2 %	50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.012 cm/cm @Thickness 3.20 mm	0.012 in/in @Thickness 0.126 in
Linear Mold Shrinkage, Transverse	0.014 cm/cm @Thickness 3.20 mm	0.014 in/in @Thickness 0.126 in

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	46.0 MPa	6670 psi	ISO 527-1/-2
Elongation at Break	115 %	115 %	ISO 527-1/-2
Elongation at Yield	4.0 %	4.0 %	ISO 527-1/-2
Tensile Modulus	1.90 GPa	276 ksi	ISO 527-1/-2
Flexural Strength	62.0 MPa	8990 psi	ISO 178
Flexural Modulus	1.80 GPa	261 ksi	ISO 178
Charpy Impact Unnotched	NB	NB	ISO 179-1
Charpy Impact, Notched	6.50 J/cm²	30.9 ft-lb/in²	ISO 179-1

Thermal Properties	Metric	English	Comments
CTE, linear	100 µm/m-°C	55.6 µin/in-°F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	95.0 °C	203 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	54.0 °C	129 °F	ISO 75-1/-2

Electrical Properties	Metric	English	Comments
Volume Resistivity	3.00e+13 ohm-cm	3.00e+13 ohm-cm	IEC 60093
Dielectric Strength	42.1 kV/mm @Thickness 1.00 mm	1070 kV/in @Thickness 0.0394 in	IEC 60243-1
Dissipation Factor	0.020 @Frequency 1.00e+6 Hz	0.020 @Frequency 1.00e+6 Hz	IEC 60250