DuPont Performance Polymers Sorona® 3030GV NC010 Polytrimethylene Terephthalate (PTT)

Category Polymer , Thermoplastic , Polyester, TP , Polytrimethylene Terephthalate (PTT)
Manufacturer DuPont Performance Polymers
Trade Name Sorona®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Sorona® 3030GV NC010 Polytrimethylene Terephthalate (PTT).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% Glass Reinforced Renewably Sourced Polytrimethylene Terephthalate Sorona 3030GV NC010 is a 30% glass reinforced PTT resin containing 25% renewably sourced ingredients by weight (37% based on polymer only) with low warpage and superior strength stifInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.56 g/cc
0.0564 lb/in³
ISO 1183
Water Absorption at Saturation 0.080 %
0.080 %
Immersion 24h; ASTM D570
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 165 MPa
23900 psi
ISO 527-1/-2
Tensile Stress 11.336 MPa

@Strain 0.300 %,
Temperature 150 °C
 1644.2 psi

@Strain 0.300 %,
Temperature 302 °F
 ISO 11403-1 -2
20.97 MPa

@Strain 0.200 %,
Temperature 0.000 °C
 3041 psi

@Strain 0.200 %,
Temperature 32.0 °F
 ISO 11403-1 -2
23.336 MPa

@Strain 0.700 %,
Temperature 150 °C
 3384.6 psi

@Strain 0.700 %,
Temperature 302 °F
 ISO 11403-1 -2
30.288 MPa

@Strain 1.00 %,
Temperature 150 °C
 4392.9 psi

@Strain 1.00 %,
Temperature 302 °F
 ISO 11403-1 -2
35.588 MPa

@Strain 1.30 %,
Temperature 150 °C
 5161.6 psi

@Strain 1.30 %,
Temperature 302 °F
 ISO 11403-1 -2
41.122 MPa

@Strain 0.400 %,
Temperature 23.0 °C
 5964.3 psi

@Strain 0.400 %,
Temperature 73.4 °F
 ISO 11403-1 -2
44.834 MPa

@Strain 0.500 %,
Temperature 40.0 °C
 6502.6 psi

@Strain 0.500 %,
Temperature 104 °F
 ISO 11403-1 -2
60.665 MPa

@Strain 0.600 %,
Temperature 0.000 °C
 8798.7 psi

@Strain 0.600 %,
Temperature 32.0 °F
 ISO 11403-1 -2
67.258 MPa

@Strain 0.800 %,
Temperature 40.0 °C
 9755.0 psi

@Strain 0.800 %,
Temperature 104 °F
 ISO 11403-1 -2
73.007 MPa

@Strain 0.700 %,
Temperature -40.0 °C
 10589 psi

@Strain 0.700 %,
Temperature -40.0 °F
 ISO 11403-1 -2
86.656 MPa

@Strain 0.900 %,
Temperature 23.0 °C
 12568 psi

@Strain 0.900 %,
Temperature 73.4 °F
 ISO 11403-1 -2
87.009 MPa

@Strain 1.10 %,
Temperature 40.0 °C
 12620 psi

@Strain 1.10 %,
Temperature 104 °F
 ISO 11403-1 -2
87.947 MPa

@Strain 0.900 %,
Temperature 0.000 °C
 12756 psi

@Strain 0.900 %,
Temperature 32.0 °F
 ISO 11403-1 -2
99.975 MPa

@Strain 1.00 %,
Temperature -40.0 °C
 14500 psi

@Strain 1.00 %,
Temperature -40.0 °F
 ISO 11403-1 -2
103.52 MPa

@Strain 1.40 %,
Temperature 40.0 °C
 15014 psi

@Strain 1.40 %,
Temperature 104 °F
 ISO 11403-1 -2
110.48 MPa

@Strain 1.20 %,
Temperature 23.0 °C
 16024 psi

@Strain 1.20 %,
Temperature 73.4 °F
 ISO 11403-1 -2
112.39 MPa

@Strain 1.20 %,
Temperature 0.000 °C
 16301 psi

@Strain 1.20 %,
Temperature 32.0 °F
 ISO 11403-1 -2
124.61 MPa

@Strain 1.30 %,
Temperature -40.0 °C
 18073 psi

@Strain 1.30 %,
Temperature -40.0 °F
 ISO 11403-1 -2
130.43 MPa

@Strain 1.50 %,
Temperature 23.0 °C
 18917 psi

@Strain 1.50 %,
Temperature 73.4 °F
 ISO 11403-1 -2
147.73 MPa

@Strain 1.60 %,
Temperature -40.0 °C
 21426 psi

@Strain 1.60 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Elongation at Break 2.5 %
2.5 %
ISO 527-1/-2
Tensile Modulus 11.0 GPa
1600 ksi
ISO 527-1/-2
Flexural Strength 245 MPa
35500 psi
ISO 178
Flexural Modulus 9.60 GPa
1390 ksi
ISO 178
Secant Modulus 3.19 GPa

@Strain 1.90 %,
Temperature 100 °C
 463 ksi

@Strain 1.90 %,
Temperature 212 °F
 ISO 11403-1 -2
3.20 GPa

@Strain 2.40 %,
Temperature 80.0 °C
 465 ksi

@Strain 2.40 %,
Temperature 176 °F
 ISO 11403-1 -2
3.71 GPa

@Strain 1.30 %,
Temperature 100 °C
 538 ksi

@Strain 1.30 %,
Temperature 212 °F
 ISO 11403-1 -2
3.84 GPa

@Strain 1.60 %,
Temperature 80.0 °C
 557 ksi

@Strain 1.60 %,
Temperature 176 °F
 ISO 11403-1 -2
4.16 GPa

@Strain 0.900 %,
Temperature 100 °C
 603 ksi

@Strain 0.900 %,
Temperature 212 °F
 ISO 11403-1 -2
4.51 GPa

@Strain 0.900 %,
Temperature 80.0 °C
 654 ksi

@Strain 0.900 %,
Temperature 176 °F
 ISO 11403-1 -2
4.7482 GPa

@Strain 0.500 %,
Temperature 100 °C
 688.68 ksi

@Strain 0.500 %,
Temperature 212 °F
 ISO 11403-1 -2
5.0068 GPa

@Strain 0.500 %,
Temperature 80.0 °C
 726.19 ksi

@Strain 0.500 %,
Temperature 176 °F
 ISO 11403-1 -2
5.4921 GPa

@Strain 0.100 %,
Temperature 100 °C
 796.57 ksi

@Strain 0.100 %,
Temperature 212 °F
 ISO 11403-1 -2
5.565 GPa

@Strain 0.100 %,
Temperature 80.0 °C
 807.1 ksi

@Strain 0.100 %,
Temperature 176 °F
 ISO 11403-1 -2
6.54 GPa

@Strain 1.90 %,
Temperature 40.0 °C
 948 ksi

@Strain 1.90 %,
Temperature 104 °F
 ISO 11403-1 -2
7.22 GPa

@Strain 1.50 %,
Temperature 40.0 °C
 1050 ksi

@Strain 1.50 %,
Temperature 104 °F
 ISO 11403-1 -2
7.661 GPa

@Strain 2.00 %,
Temperature 23.0 °C
 1111 ksi

@Strain 2.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
7.91 GPa

@Strain 1.10 %,
Temperature 40.0 °C
 1150 ksi

@Strain 1.10 %,
Temperature 104 °F
 ISO 11403-1 -2
8.50 GPa

@Strain 1.80 %,
Temperature 0.000 °C
 1230 ksi

@Strain 1.80 %,
Temperature 32.0 °F
 ISO 11403-1 -2
8.51 GPa

@Strain 1.60 %,
Temperature 23.0 °C
 1230 ksi

@Strain 1.60 %,
Temperature 73.4 °F
 ISO 11403-1 -2
8.57 GPa

@Strain 0.700 %,
Temperature 40.0 °C
 1240 ksi

@Strain 0.700 %,
Temperature 104 °F
 ISO 11403-1 -2
8.59 GPa

@Strain 2.10 %,
Temperature -40.0 °C
 1250 ksi

@Strain 2.10 %,
Temperature -40.0 °F
 ISO 11403-1 -2
9.11 GPa

@Strain 1.70 %,
Temperature -40.0 °C
 1320 ksi

@Strain 1.70 %,
Temperature -40.0 °F
 ISO 11403-1 -2
9.21 GPa

@Strain 1.20 %,
Temperature 23.0 °C
 1340 ksi

@Strain 1.20 %,
Temperature 73.4 °F
 ISO 11403-1 -2
9.23 GPa

@Strain 1.30 %,
Temperature 0.000 °C
 1340 ksi

@Strain 1.30 %,
Temperature 32.0 °F
 ISO 11403-1 -2
9.32 GPa

@Strain 0.100 %,
Temperature 40.0 °C
 1350 ksi

@Strain 0.100 %,
Temperature 104 °F
 ISO 11403-1 -2
9.59 GPa

@Strain 1.30 %,
Temperature -40.0 °C
 1390 ksi

@Strain 1.30 %,
Temperature -40.0 °F
 ISO 11403-1 -2
9.77 GPa

@Strain 0.900 %,
Temperature 0.000 °C
 1420 ksi

@Strain 0.900 %,
Temperature 32.0 °F
 ISO 11403-1 -2
9.98 GPa

@Strain 0.700 %,
Temperature 23.0 °C
 1450 ksi

@Strain 0.700 %,
Temperature 73.4 °F
 ISO 11403-1 -2
10.1 GPa

@Strain 0.900 %,
Temperature -40.0 °C
 1470 ksi

@Strain 0.900 %,
Temperature -40.0 °F
 ISO 11403-1 -2
10.3 GPa

@Strain 0.500 %,
Temperature 0.000 °C
 1490 ksi

@Strain 0.500 %,
Temperature 32.0 °F
 ISO 11403-1 -2
10.45 GPa

@Strain 0.100 %,
Temperature 23.0 °C
 1516 ksi

@Strain 0.100 %,
Temperature 73.4 °F
 ISO 11403-1 -2
10.59 GPa

@Strain 0.100 %,
Temperature 0.000 °C
 1536 ksi

@Strain 0.100 %,
Temperature 32.0 °F
 ISO 11403-1 -2
11.022 GPa

@Strain 0.100 %,
Temperature -40.0 °C
 1598.6 ksi

@Strain 0.100 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Charpy Impact Unnotched 5.00 J/cm²
23.8 ft-lb/in²
ISO 179/1eU
4.50 J/cm²

@Temperature -30.0 °C
 21.4 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
ISO 179/1eA
0.900 J/cm²

@Temperature -30.0 °C
 4.28 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance 8.00e+13 ohm
8.00e+13 ohm
IEC 60093