DuPont Performance Polymers Delrin® 988PA NC010 Acetal Homopolymer (Unverified Data**)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Delrin® 988PA NC010 Acetal Homopolymer
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Delrin® 988PA NC010 is a low viscosity acetal homopolymer for injection molding with low screw deposit. It is especially formulated for gear applications requiring high precision and dimensional stability.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.020 cm/cm | 0.020 in/in | 50 X 2mm pulley |
| 0.016 cm/cm @Thickness 3.20 mm |
0.016 in/in @Thickness 0.126 in |
Flow | |
| 0.017 cm/cm @Thickness 3.20 mm |
0.017 in/in @Thickness 0.126 in |
Transverse | |
| Melt Flow | 25 g/10 min @Load 2.16 kg, Temperature 190 °C |
25 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 72.0 MPa @Temperature 23.0 °C |
10400 psi @Temperature 73.4 °F |
ISO 527 |
| Elongation at Break | 27 % @Temperature 23.0 °C |
27 % @Temperature 73.4 °F |
ISO 527 |
| Elongation at Yield | 12 % @Temperature 23.0 °C |
12 % @Temperature 73.4 °F |
ISO 527 |
| Tensile Modulus | 3.00 GPa @Temperature 23.0 °C |
435 ksi @Temperature 73.4 °F |
ISO 527 |
| Flexural Modulus | 3.00 GPa @Temperature 23.0 °C |
435 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.630 J/cm² @Temperature 23.0 °C |
3.00 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 178 °C | 352 °F | 10°C/min; ISO 11357-1/-3 |
| UL RTI, Electrical | 50.0 °C @Thickness 0.800 mm |
122 °F @Thickness 0.0315 in |
UL 746B |
| 50.0 °C @Thickness 3.00 mm |
122 °F @Thickness 0.118 in |
UL 746B | |
| UL RTI, Mechanical with Impact | 50.0 °C @Thickness 3.00 mm |
122 °F @Thickness 0.118 in |
UL 746B |
| 50.0 °C @Thickness 0.800 mm |
122 °F @Thickness 0.0315 in |
UL 746B | |
| UL RTI, Mechanical without Impact | 50.0 °C @Thickness 0.800 mm |
122 °F @Thickness 0.0315 in |
UL 746B |
| 50.0 °C @Thickness 3.00 mm |
122 °F @Thickness 0.118 in |
UL 746B | |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
UL94 |
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL94 | |
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
UL94 | |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
IEC 60695-11-10 | |
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC 60695-11-10 | |
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
IEC 60695-11-10 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 210 °C | 392 - 410 °F | Injection Molding |
| 205 °C | 401 °F | Optimum; Injection Molding | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Injection Molding |
| 70.0 °C | 158 °F | optimum; Injection Molding | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Injection Molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Forms | Pellets | |
| Generic | Acetal (POM) Homopolymer | |
| Material Status | Preliminary Data | |
| Part Marking Code | >POM< | ISO 11469 |
| Processing Method | Injection Molding | |
| Product Category | Unreinforced Resins | |
| Resin Identification | POM | ISO 1043 |
| RoHS Compliance | Contact Manufacturer |