Dow DNDA-1082 NT 7 Linear Low Density Polyethylene Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE
Manufacturer Dow Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow DNDA-1082 NT 7 Linear Low Density Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DOW DNDA-1082 NT 7 is produced using UNIPOL™ PE process technology. It is intended for high-speed injection molding of thin walled parts such as downguaged lids. Information provided by Dow
Physical Properties Metric English Comments
Density 0.933 g/cc
0.0337 lb/in³
ASTM D792
Melt Index of Compound 155 g/10 min

@Load 2.16 kg,
Temperature 190 °C
155 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 52
52
Molded and tested in accordance with ASTM D4976; ASTM D2240
Tensile Strength at Break 8.96 MPa
1300 psi
Molded and tested in accordance with ASTM D4976; ASTM D638
Tensile Strength, Yield 16.5 MPa
2400 psi
Molded and tested in accordance with ASTM D4976; ASTM D638
Elongation at Break 50 %
50 %
Molded and tested in accordance with ASTM D4976; ASTM D638
Elongation at Yield 8.0 %
8.0 %
Molded and tested in accordance with ASTM D4976; ASTM D638
Flexural Modulus 0.572 GPa
83.0 ksi
2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 B
Tensile Impact Strength 105 kJ/m²
50.0 ft-lb/in²
Molded and tested in accordance with ASTM D4976; ASTM D1822, Type S
Thermal Properties Metric English Comments
Melting Point 125 °C
257 °F
Dow Method (DSC)
Crystallization Temperature 113 °C
235 °F
Dow Method (DSC)
Deflection Temperature at 0.46 MPa (66 psi) 52.2 °C
126 °F
Molded and tested in accordance with ASTM D4976; ASTM D648
Vicat Softening Point 122 °C
252 °F
ASTM D1525
Brittleness Temperature -20.0 °C
-4.00 °F
Molded and tested in accordance with ASTM D4976; ASTM D746