| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 °C | 126 °F | injection molded specimen; ASTM D648 |
| Phillips Sumika Marlex® CHP-035 Thermoplastic Polyolefin
(discontinued **) Applications: Painted air-bag coversSoft interior trimSoft touch overmoldingInformation provided by Chevron Phillips.Phillips Sumika Polypropylene Company has been shut down, as announced in 2011. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 °C | 126 °F | ASTM D648 |
| ExxonMobil Escorene® LL-8461 LLDPE, Rotational Molding Powder
(discontinued **) Data Provided by Exxon Chemical Canada.Characteristics: Fully formulated, UV-8 type protection, Good stiffnessUses: Septic tanks, Chemical storage bins, Potable water tanks |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 - 61.0 °C | 126 - 142 °F | ASTM D648 |
| DSM Somos® 9120 Epoxy Photopolymer
(Unverified Data**) DescriptionDSM Somos® 9120 is a liquid photopolymer that produces robust, functional and accurate parts using stereolithography machines. The material offers superior chemical resistance, a wide p.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 °C | 126 °F | ASTM D648 |
| LyondellBasell Petrothene® GA594189 Linear Low Density Polyethylene, Injection Molding Grade PETROTHENE GA594189 is a pelletized LLDPE copolymer resin for injection molding thin-walled items requiring high flow and short cycle times. GA594189 exhibits excellent flow, warp resistance and sur.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 °C | 126 °F | ASTM D648 |
| SK Chemicals SKYPEL P128DW Productivity Grade SKYPEL is a thermoplastic polyester elastomer (TPEE). It is a polymer resin having the property somewhere between plastics and rubber, which have various properties ranging from high hardness plasti.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 °C @Thickness 3.20 mm |
126 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 396 Ionomer DescriptionFormion® FI 3936is a 3% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, and impact. Formion F1 396U is UV stabilized to exceed .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 °C | 126 °F | ASTM D648 |
| A. Schulman POLYAXIS® LP624 Stabilized High Density Polyethylene DescriptionPolyaxis CP 624 is a stabilized high density polyethylene rotational molding compound with good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 °C @Thickness 3.20 mm |
126 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 396 Ionomer DescriptionFormion® FI 3936is a 3% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, and impact. Formion F1 396U is UV stabilized to exceed .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 °C | 126 °F | ASTM D648 |
| A. Schulman POLYAXIS® LP624 Stabilized High Density Polyethylene DescriptionPolyaxis CP 624 is a stabilized high density polyethylene rotational molding compound with good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 °C | 126 °F | ASTM D648 |
| A. Schulman POLYAXIS® LP624 Stabilized High Density Polyethylene DescriptionPolyaxis CP 624 is a stabilized high density polyethylene rotational molding compound with good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 °C @Thickness 3.20 mm |
126 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 396 Ionomer DescriptionFormion® FI 3936is a 3% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, and impact. Formion F1 396U is UV stabilized to exceed .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 °C | 126 °F | ASTM D648 |
| A. Schulman POLYAXIS® LP624 Stabilized High Density Polyethylene DescriptionPolyaxis CP 624 is a stabilized high density polyethylene rotational molding compound with good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 °C @Thickness 3.20 mm |
126 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 396 Ionomer DescriptionFormion® FI 3936is a 3% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, and impact. Formion F1 396U is UV stabilized to exceed .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 °C | 126 °F | ISO 75 |
| Unitika TERRAMAC TP-4030 Polylactic Acid (PLA) Soft, Extrusion, blow, and foam sheet grade. Bio-based materials produced from annually renewable raw materials.Information provided by Unitika Ltd. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 °C @Thickness 3.20 mm |
126 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 396 Ionomer DescriptionFormion® FI 3936is a 3% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, and impact. Formion F1 396U is UV stabilized to exceed .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 °C | 126 °F | ASTM D648 |
| A. Schulman POLYAXIS® LP624 Stabilized High Density Polyethylene DescriptionPolyaxis CP 624 is a stabilized high density polyethylene rotational molding compound with good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 °C @Thickness 3.20 mm |
126 °F @Thickness 0.126 in |
ISO 75 |
| A. Schulman FORMION™ FI 396 Ionomer DescriptionFormion® FI 3936is a 3% glass fiber reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, and impact. Formion F1 396U is UV stabilized to exceed .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 °C | 126 °F | |
| Eastman Ecdel PCCE 9966 Copolyester Ether Elastomer ISO data as provided by the manufacturer, Eastman Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 - 61.0 °C | 126 - 142 °F | ASTM D648-07 |
| DSM Somos® 9120 The need for movable parts is a constant when it comes to prototyping. Being able to ensure the proper fit for parts within a component can save both time and money. Somos® 9120 creates semi-transp.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.2 °C | 126 °F | ASTM D648 |
| ExxonMobil LLDPE LL 8446.21 Linear Low Density Polyethylene Resin (European Grade) Product Description: LL 8446 is a linear low density butane copolymer designed to offer excellent processability, whiteness, and fast grinding rate. This UV stabilized resin is ideally suited for ap.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.2 °C | 126 °F | Molded and tested in accordance with ASTM D4976; ASTM D648 |
| Dow DNDA-1082 NT 7 Linear Low Density Polyethylene Resin DOW DNDA-1082 NT 7 is produced using UNIPOL™ PE process technology. It is intended for high-speed injection molding of thin walled parts such as downguaged lids. Information provided by Dow |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 °C | 126 °F | ASTM D648 |
| Arkema Group Pebax® 4033 Polyether Block Amide (PEBA) Typical application: Mechanical partsInformation provided by Arkema Group |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 °C | 126 °F | |
| Arkema Group Pebax® 4033 SN 01 Polyether Block Amide (PEBA) (Conditioned) POLYETHER BLOCK AMIDE (PEBA) hardness 40 shore D Non plasticized flexible Polyamide Outstanding mechanical properties at low temperature (-40°C) Applications: molded parts for sport goods (softness.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.2 °C | 126 °F | ASTM D648 |
| Aclo Accutech Polypropylene Copolymer CP0436C20L1 Calcium Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.2 °C | 126 °F | ASTM D648 |
| Aclo Accutech Polypropylene Copolymer CP0436C30L1 Calcium Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 °C | 126 °F | ASTM D648 |
| A. Schulman POLYAXIS® LP624 Stabilized High Density Polyethylene DescriptionPolyaxis CP 624 is a stabilized high density polyethylene rotational molding compound with good flow and stiffness. NOTE: Physical properties are based on rotationally molded samples from.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 - 142 °C | 126 - 288 °F | Average value: 76.3 °C Grade Count:21 |
| Overview of materials for High Density Polyethylene (HDPE), Rotational Molding Grade This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Rotational Molding Grade". Each property range of values reported is m.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 °C | 126 °F | ASTM D648 |
| Arkema Group Pebax® MX 1205 Polyether Block Amide (PEBA) Typical application: Impact modifierInformation provided by Arkema Group |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 °C | 126 °F | |
| Arkema Group Pebax® MX 1205 SN 01 Polyether Block Amide (PEBA) (Conditioned) POLYETHER BLOCK AMIDE (PEBA) hardness 40 shore D Non plasticized flexible Polyamide Outstanding mechanical properties at low temperature (-40°C) Applications: molded parts for sport goods (softness.. |
|||