Braskem TS7006 LDPE Blown Film Extrusion Polyethylene
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | Braskem |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Braskem TS7006 LDPE Blown Film Extrusion Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
TS7006 is a low-density polyethylene (LDPE) specially developed for coextruded films and lamination. The resin presents a combination of mechanical, optical, and stiffness properties. TS7006 has a low gels content which ensures production of excellent appearance films. This product is identified as PE 114 according to ASTM D-4976-04a standard specification. It contains antiblocking and slip agent additives. Its applications include high clarity films for coextruded food packaging (cheese, meat, sausages, sliced ham, etc.).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ASTM-D792 |
| Melt Flow | 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.60 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 350 % | 350 % | ASTM-D882 |
| Film Elongation at Break, TD | 700 % | 700 % | ASTM-D882 |
| Secant Modulus, MD | 0.140 GPa | 20.3 ksi | 2% Secant Modulus; ASTM-D882 |
| Secant Modulus, TD | 0.170 GPa | 24.7 ksi | 2% Secant Modulus; ASTM-D882 |
| Elmendorf Tear Strength MD | 310 g | 310 g | ASTM-D1922 |
| Elmendorf Tear Strength TD | 250 g | 250 g | ASTM-D1922 |
| Elmendorf Tear Strength, MD | 6.20 g/micron | 157 g/mil | ASTM-D1922 |
| Elmendorf Tear Strength, TD | 5.00 g/micron | 127 g/mil | ASTM-D1922 |
| Dart Drop | 3.40 g/micron | 86.4 g/mil | ASTM-D1709 |
| Dart Drop Test | 170 g | 0.375 lb | ASTM-D1709 |
| Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ASTM-D882 |
| Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ASTM-D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 9.0 % | 9.0 % | ASTM-D1003 |
| Gloss | 60 % | 60 % | Angle 45°; ASTM-D2457 |
| 84 % | 84 % | Angle 60°; ASTM-D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Die Opening | 0.100 cm | 0.0394 in | Blow Film Extrusion |
| Blow-up Ratio (BUR) | 2.0 - 3.0 | 2.0 - 3.0 | Blow Film Extrusion |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Mass Temperature (°C) | 180-185 | Blow Film Extrusion |
| Temperature Profile (°C) | 150-185 | Blow Film Extrusion |
Users viewing this material also viewed the following:
- LNP Thermocomp® UF-1006 HS Polyphthalamide, Glass Fiber Reinforcement (discontinued **)
- Karina E 1000/HMB 21586 White Concentrate Color Concentrate
- Heatbath/Park Pen Karb Deepcase Carburizer
- SSAB Tunnplat Domex® 014 BOR Oil quenched Boron Steel
- Shinil Chemical SHINNANO PP Polymer Nanocomposite Door Trim
- Zotefoams Plastazote® LD33FM Low Density Polyethylene Foam, Flame Retarded
- Lubrizol Estane® AG 9550 Thermoplastic Polyurethane
- DuPont™ Nomex® N196 Paper, 20 mil Nominal Thickness
- Beijing Evergrow Resources PTFE, 15% Carbon Fiber Filled
Copyright © lookpolymers.com All Rights Reserved