Braskem Pluris 9310 LLDPE Blown Film Extrusion Polyethylene Quatropolymer
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | Braskem |
| Trade Name | Pluris |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Braskem Pluris 9310 LLDPE Blown Film Extrusion Polyethylene Quatropolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Pluris 9310 is a Braskem Quatropolymer produced with Spherilene technology and is a LLDPE with unique properties, such as high stiffness associated with toughness. It is easier to process than conventional LLDPE with the same melt index and shows very good bubble stability. Films obtained with this product have very low gel content. It contains medium antiblocking, medium slip, and medium processing aid additives. Its applications include: automatic packaging (FFS), high performance structures (coextrusion), and frozen bags.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM-D792 |
| Melt Flow | 0.55 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.55 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 890 % | 890 % | ASTM-D882 |
| Film Elongation at Break, TD | 1110 % | 1110 % | ASTM-D882 |
| Elmendorf Tear Strength MD | 270 g | 270 g | ASTM-D1922 |
| Elmendorf Tear Strength TD | 590 g | 590 g | ASTM-D1922 |
| Elmendorf Tear Strength, MD | 7.11 g/micron | 181 g/mil | ASTM-D1922 |
| Elmendorf Tear Strength, TD | 15.53 g/micron | 394.5 g/mil | ASTM-D1922 |
| Dart Drop | 30.26 g/micron | 768.6 g/mil | ASTM-D1709 |
| Dart Drop Test | 1150 g | 2.54 lb | ASTM-D1709 |
| Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM-D882 |
| Film Tensile Strength at Break, TD | 40.0 MPa | 5800 psi | ASTM-D882 |
| 1% Secant Modulus, MD | 270 MPa | 39200 psi | ASTM-D882 |
| 1% Secant Modulus, TD | 310 MPa | 45000 psi | ASTM-D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 16 % | 16 % | ASTM-D1003 |
| Gloss | 75 % | 75 % | Angle 60°; ASTM-D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Die Opening | 0.180 - 0.250 cm @Temperature 200 - 220 °C |
0.0709 - 0.0984 in @Temperature 392 - 428 °F |
Blown Film Extrusion |
| Blow-up Ratio (BUR) | 2.0 - 3.5 | 2.0 - 3.5 | Blown Film Extrusion |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Mass Temperature (°C) | 220 | max, Blown Film Extrusion |
| Screen Package | 40/60/40 | mesh |
| Temperature Profile (°C) | 190-220 | Blown Film Extrusion |