Polymer Property : Film Tensile Strength at Break, TD = 40.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ISO 527-3
Polimeri Europa Clearflex® H&T CLH 108 Octene Copolymer Linear Low Density Polyethylene
Clearflex H&T CLH 108 is an octene copolymer linear low density polyethylene (C8-LLDPE), with antioxidants, suitable for cast film extrusion. Stretch films obtained from Clearflex H&T CLH 108 show e..
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ASTM D882
SABIC 6821N Linear Low Density Polyethylene for Blown Film
Product Description: 6821N is a fractional melt index hexene copolymer based Linear Low Density Polyethylene grade suitable for high strength packaging applications. Films produced using this resi..
Film Tensile Strength at Break, TD 40.0 MPa

@Thickness 0.400 mm
5800 psi

@Thickness 0.0157 in
ISO 527
Premix Thermoplastics PRE-ELEC® PS 1331 Carbon Black Filled Conductive Thermoplastic Compound
PRE-ELEC® PS 1331 is a carbon black filled conductive thermoplastic compound based on polystyrene. In addition to a low electrical resistivity PRE-ELEC® PS 1331 has excellent mechanical properties..
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ISO 527-3
Polimeri Europa Clearflex® FF 508 Octene Copolymer Linear Medium Density Polyethylene
Clearflex FF 508 is an octene copolymer linear medium density polyethylene (C8-LMDPE), with antioxidants and processing aid, suitable for blown film extrusion.Films manufactured with Clearflex FF 50..
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ISO 527-3
Polimeri Europa Clearflex® H&T LGH 138 Octene Copolymer Linear Low Density Polyethylene
Clearflex H&T LGH 138 is an octene copolymer linear low density polyethylene (C8-LLDPE), with antioxidants, slip agent, antiblocking and processing aid, suitable for blown film extrusion.Films obtai..
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ASTM D882
Chevron Phillips 6120 LLDPE Cast/Blown Film Resin, Butene Copolymer  (discontinued **)
Resin Type: Butene CopolymerCharacteristics: Good Stiffness at Thin Gauges, Good Optics, Good Drawdown, Can be used straight or blended with LDPE or HDPE, Can be used in blown or cast applicationsAp..
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ASTM D882
Chevron Phillips 7109BKT LLDPE Blown Film Resin, Hexene Copolymer  (discontinued **)
Resin Type: Hexene Copolymer, Medium Slip, Medium Antiblock Version of 7109TCharacteristics: Good Stiffness at Thin Gauges, Good Drawdown, Low COF, Can be used straight or blended with LDPE or HDPE...
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ISO 527
Total Finathene® LL 6010 FE 18P LLDPE film  (discontinued **)
Linear low density polyethylene made by gas phase process for blown film applications. Advised temperature profile: 190 to 220°C.Information provided provided by Total Petrochemicals.Total Petroche..
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ASTM D882
ExxonMobil Escorene® LD-768 High EVA Film and Compounding Resin  (discontinued **)
Data provided by the manufacturer, Exxon Chemical.A low gel 27.5% vinyl acetate copolymer designed for film and compounding applications. The resin provides very low modulus films with high tensile..
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ASTM D882
Reliance Industries Reclair O21010 Polyethylene
Octene comonomer based Linear Low Density Polyethylene. Blow film grade. Contains an optimum level of antioxidants and polymer processing aids. Designed for lamination film applications. Character..
Film Tensile Strength at Break, TD <= 40.0 MPa
<= 5800 psi
ISO 527
Iran Petrochemical (PCC) EX 4HS HM 9455 F1 High Density Polyethylene
EX 4HS is a high density polyethylene with 1-Butene as co monomer. It has high rigidity, low gel level, high drawdown, very high stiffness and good tenacity.Applications: film extrusion, blending ..
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
UBE 5034FDX33 Air Blown Nylon 6/66 Film
Specialties: High transparencyLow neck-inNucleated typeApplications: Suitable for T-die,Water and Air blown process Processing: Shrink bags (Water) Pouch ( Air blown) Information provided by UBE.
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ISO 527-3
Borealis Borstar® FB4230 LLDPE for Film
Borstar FB4250T is a high molecular weight linear low density polyethylene grade combining good extrusion properties, excellent draw properties and good mechanical strength. Film made from Borstar ..
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ASTM D882
ExxonMobil NTX™ NTX 095 Super Strength Film Resin
NTX super strength hexene blown film resins are designed for applications requiring exceptional strength for maximum downgauging potential. Key property improvements are significantly superior impac..
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ASTM D882
ExxonMobil NTX™ NTX 104 Super Strength Film Resin
NTX super strength hexene blown film resins are designed for applications requiring exceptional strength for maximum downgauging potential. Key property improvements are significantly superior impac..
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ASTM D882
ExxonMobil NTX™ NTX 141 Super Strength Film Resin
NTX super strength hexene blown film resins are designed for applications requiring exceptional strength for maximum downgauging potential. Key property improvements are significantly superior impac..
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ASTM D882
Dow DOWLEX™ 2025G Linear Low Density Polyethylene
DOWLEX™ 2025G is a medium modulus resin with excellent toughness properties designed for thin film applications.Information provided by Dow
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ASTM D882
Braskem Green PE SLH118 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene
Description: SLH118 is a Linear Low Density Polyethylene, copolymer of hexene-1. Developed for blown film extrusion in blends with polyethylenes. Films obtained with this product show a good process..
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ASTM D882
Braskem Green PE SLH218 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene
Description: SLH218 is a LLDPE Hexene copolymer produced by Braskem. It shows a good balance between optical properties, mechanical properties (Mainly stretchability), sealability and processability..
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ASTM-D882
Braskem LF118 LLDPE Blown Film Extrusion Polyethylene Copolymer
LF118 is a linear low-density polyethylene, copolymer of butene-1, produced by the gas phase process. It is developed for blown film extrusion in blends with polyethylene. Films obtained with this p..
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ASTM D882
Braskem LH0820/30AF Blown Film Extrusion Linear Low Density Polyethylene
Description: LH0820/30AF is a LLDPE hexene copolymer produced by Braskem. It offers outstanding processability combined with excellent mechanical properties. Very low gel amount.Applications: Lamina..
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ASTM D882
Braskem LH118 Blown Film Extrusion Linear Low Density Polyethylene
Stretch films; Liners; LDPE and HDPE blends; Packages for general use.Information provided by Braskem.
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ASTM D882
Braskem LH218 Cast Film Extrusion Linear Low Density Polyethylene
Description: LH218 is a LLDPE Hexene copolymer produced by Braskem. It shows a good balance between optical properties, mechanical properties (Mainly stretchability), sealability and processability...
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ASTM-D882
Braskem LL5800N LLDPE Blown Film Extrusion Polyethylene Copolymer
LL5800N resin is a linear low-density polyethylene, copolymer of octene-1, produced by the solution process for blown film extrusion with excellent mechanical properties. It contains processing aid ..
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ASTM-D882
Braskem LL5801N LLDPE Blown Film Extrusion Polyethylene Copolymer
The LL5801N resin is a linear low-density polyethylene, copolymer of octene-1, produced by the solution process for blown film extrusion with excellent mechanical properties. It contains processing ..
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ASTM-D882
Braskem LL6800N LLDPE Blown Film Extrusion Polyethylene Copolymer
LL6800N resin is a linear low-density polyethylene, copolymer of octene-1, produced by the solution process for blown film extrusion with excellent mechanical properties. It contains antiblock, proc..
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ASTM-D882
Braskem Pluris 9300 LLDPE Blown Film Extrusion Polyethylene Quatropolymer
Pluris 9300 is a Quatropolymer produced with Spherilene technology and is a LLDPE with unique properties, such as high stiffness associated with toughness. It is easier to process than conventional ..
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ASTM D882
Braskem Green PE SLH0820/30AF Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene
Description: SLH0820/30AF is a LLDPE hexene copolymer produced by Braskem. It offers outstanding processability combined with excellent mechanical properties. Very low gel amount. The minimum biobas..
Film Tensile Strength at Break, TD 40.0 MPa
5800 psi
ASTM D882
Braskem Green PE SLL118 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene
Description: SLL118 is a Linear Low Density Polyethylene, copolymer of butene-1. Developed for blown film extrusion in blends with polyethylenes. Films obtained with this product show a good process..
Film Tensile Strength at Break, TD 40.0 - 46.0 MPa
5800 - 6670 psi
Average value: 42.3 MPa Grade Count:4
Overview of materials for High Density Polyethylene (HDPE), Extruded
This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Extruded". Each property range of values reported is minimum and maxim..