Bhansali Engineering Abstron IM-17 A EP ABS Electro Plating Applications

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Plating Grade
Manufacturer Bhansali Engineering
Trade Name Abstron
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Bhansali Engineering Abstron IM-17 A EP ABS Electro Plating Applications.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Electroplating & Hot Stamping GradesInformation provided by Bhansali
Physical Properties Metric English Comments
Density 1.045 g/cc
0.03775 lb/in³
ASTM D-792
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
ASTM D-955
Melt Flow 45 g/10 min
<br>@Load 10.0 kg,<br> Temperature 220 °C
 45 g/10 min
<br>@Load 22.0 lb,<br> Temperature 428 °F
 ASTM D-1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 110
110
ASTM D-785
Tensile Strength, Yield 41.7 MPa
<br>@Thickness 3.20 mm
 6040 psi
<br>@Thickness 0.126 in
 Type 1, 5 mm/min speed; ASTM D-638
Flexural Yield Strength 58.8 MPa
<br>@Thickness 6.40 mm
 8530 psi
<br>@Thickness 0.252 in
 ASTM D-790
Flexural Modulus 1.96 GPa
<br>@Thickness 6.40 mm
 284 ksi
<br>@Thickness 0.252 in
 ASTM D-790
Izod Impact, Notched 1.8627 J/cm
<br>@Thickness 6.40 mm
 3.4896 ft-lb/in
<br>@Thickness 0.252 in
 ASTM D-256
2.2549 J/cm
<br>@Thickness 3.20 mm
 4.2244 ft-lb/in
<br>@Thickness 0.126 in
 ASTM D-256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
Method A - Annealed; ASTM D-648
Vicat Softening Point 104 °C
219 °F
Method B; ASTM D-1525
Flammability, UL94 HB
<br>@Thickness 3.20 mm
 HB
<br>@Thickness 0.126 in
 UL-94