DuPont Performance Polymers Minlon® 12TA BKB124 Nylon 66  (Unverified Data**)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Mineral Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Minlon® 12TA BKB124 Nylon 66  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Minlon® 12TA BKB124 is a 32% mineral reinforced, toughened, heat stabilized, black polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Specific Gravity 1.38 g/cc
1.38 g/cc
DAM; ASTM D792
Density 1.38 g/cc
0.0499 lb/in³
DAM; ISO 1183
Filler Content 32 %
32 %
DAM
Linear Mold Shrinkage 0.010 cm/cm

@Thickness 1.60 mm
0.010 in/in

@Thickness 0.0630 in
Flow; DAM
0.010 cm/cm

@Thickness 3.20 mm
0.010 in/in

@Thickness 0.126 in
Flow; DAM
0.010 cm/cm

@Thickness 1.60 mm
0.010 in/in

@Thickness 0.0630 in
Transverse; DAM
0.010 cm/cm

@Thickness 3.20 mm
0.010 in/in

@Thickness 0.126 in
Transverse; DAM
0.015 cm/cm

@Thickness 6.40 mm
0.015 in/in

@Thickness 0.252 in
Flow; DAM
0.015 cm/cm

@Thickness 6.40 mm
0.015 in/in

@Thickness 0.252 in
Transverse; DAM
Mechanical Properties Metric English Comments
Tensile Strength at Break 58.0 MPa

@Temperature 23.0 °C
8410 psi

@Temperature 73.4 °F
50%RH; ISO 527
78.0 MPa

@Temperature 23.0 °C
11300 psi

@Temperature 73.4 °F
DAM; ISO 527
Tensile Strength 76.0 MPa

@Temperature 23.0 °C
11000 psi

@Temperature 73.4 °F
DAM; ASTM D638
Elongation at Break 15 %

@Temperature 23.0 °C
15 %

@Temperature 73.4 °F
DAM; ISO 527
17 %

@Temperature 23.0 °C
17 %

@Temperature 73.4 °F
DAM; ASTM D638
40 %

@Temperature 23.0 °C
40 %

@Temperature 73.4 °F
50%RH; ISO 527
Tensile Modulus 1.90 GPa

@Temperature 23.0 °C
276 ksi

@Temperature 73.4 °F
50%RH; ISO 527
4.80 GPa

@Temperature 23.0 °C
696 ksi

@Temperature 73.4 °F
DAM; ISO 527
Flexural Modulus 1.80 GPa

@Temperature 23.0 °C
261 ksi

@Temperature 73.4 °F
50%RH; ISO 178
4.40 GPa

@Temperature 23.0 °C
638 ksi

@Temperature 73.4 °F
DAM; ISO 178
4.41 GPa

@Temperature 23.0 °C
640 ksi

@Temperature 73.4 °F
DAM; ASTM D790
Izod Impact, Notched 0.800 J/cm

@Temperature 23.0 °C
1.50 ft-lb/in

@Temperature 73.4 °F
DAM; ASTM D256
Izod Impact, Unnotched 16.0 J/cm

@Temperature 23.0 °C
30.0 ft-lb/in

@Temperature 73.4 °F
DAM; ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature -40.0 °C
2.38 ft-lb/in²

@Temperature -40.0 °F
DAM; ISO 180/1A
6.00 kJ/m²

@Temperature -40.0 °C
2.86 ft-lb/in²

@Temperature -40.0 °F
50%RH; ISO 180/1A
6.00 kJ/m²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
DAM; ISO 180/1A
6.00 kJ/m²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
50%RH; ISO 180/1A
7.00 kJ/m²

@Temperature 23.0 °C
3.33 ft-lb/in²

@Temperature 73.4 °F
DAM; ISO 180/1A
12.0 kJ/m²

@Temperature 23.0 °C
5.71 ft-lb/in²

@Temperature 73.4 °F
50%RH; ISO 180/1A
Izod Impact, Unnotched (ISO) 85.0 kJ/m²

@Temperature -30.0 °C
40.4 ft-lb/in²

@Temperature -22.0 °F
DAM; ISO 180/1U
85.0 kJ/m²

@Temperature -30.0 °C
40.4 ft-lb/in²

@Temperature -22.0 °F
50%RH; ISO 180/1U
110 kJ/m²

@Temperature 23.0 °C
52.3 ft-lb/in²

@Temperature 73.4 °F
DAM; ISO 180/1U
330 kJ/m²

@Temperature 23.0 °C
157 ft-lb/in²

@Temperature 73.4 °F
50%RH; ISO 180/1U
Charpy Impact Unnotched 7.50 J/cm²

@Temperature -30.0 °C
35.7 ft-lb/in²

@Temperature -22.0 °F
DAM; ISO 179/1eU
8.00 J/cm²

@Temperature -30.0 °C
38.1 ft-lb/in²

@Temperature -22.0 °F
50%RH; ISO 179/1eU
12.0 J/cm²

@Temperature 23.0 °C
57.1 ft-lb/in²

@Temperature 73.4 °F
DAM; ISO 179/1eU
33.0 J/cm²

@Temperature 23.0 °C
157 ft-lb/in²

@Temperature 73.4 °F
50%RH; ISO 179/1eU
Charpy Impact, Notched 0.300 J/cm²

@Temperature -40.0 °C
1.43 ft-lb/in²

@Temperature -40.0 °F
50%RH; ISO 179/1eA
0.400 J/cm²

@Temperature -40.0 °C
1.90 ft-lb/in²

@Temperature -40.0 °F
DAM; ISO 179/1eA
0.400 J/cm²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
50%RH; ISO 179/1eA
0.500 J/cm²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
DAM; ISO 179/1eA
0.700 J/cm²

@Temperature 23.0 °C
3.33 ft-lb/in²

@Temperature 73.4 °F
DAM; ISO 179/1eA
1.20 J/cm²

@Temperature 23.0 °C
5.71 ft-lb/in²

@Temperature 73.4 °F
50%RH; ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 257 °C
495 °F
10°C/min; DAM; ISO 11357-1/-3
258 °C
496 °F
DAM; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
167 °F
DAM; ASTM D648
80.0 °C
176 °F
DAM; ISO 75-1/-2
Processing Properties Metric English Comments
Melt Temperature 295 °C
563 °F
DAM; Optimum
285 - 305 °C
545 - 581 °F
DAM
Mold Temperature 70.0 - 120 °C
158 - 248 °F
DAM
100 °C
212 °F
DAM; optimum
Drying Temperature 80.0 °C
176 °F
DAM
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
DAM
Moisture Content <= 0.20 %
<= 0.20 %
DAM
Descriptive Properties Value Comments
Additive Impact Modifier
DAM
Appearance Black Color
DAM
Drying Recommended Yes, if moisture content of resin exceeds recommended level
DAM
Features Impact Resistance, Good
DAM
Warpage, Low
DAM
Filler Mineral filler
DAM
Forms Pellets
DAM
Generic Nylon 66
DAM
Heat Stabilized Yes
DAM
Material Status Current
DAM
Part Marking Code >PA66-IMD32<
ISO 11469; DAM
Polymer Family Polyamide
DAM
Polymer Type PA66
DAM
Processing Method Injection Molding
DAM
Product Category Low Warp Resins
DAM
Mineral Reinforced Resins
DAM
Toughened Resins
DAM
Resin Identification PA66-IMD32
ISO 1043; DAM
RoHS Compliance Contact Manufacturer
DAM
Uses Appliance Components
DAM
Automotive Applications
DAM
Tool, Power & Others
DAM