Beijing Ranger Chem PBT-201-G30 272 Flame Retarding FR PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled , Polybutylene Terephthalate (PBT), Flame Retardant
Manufacturer Beijing Ranger Chemical Co
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Beijing Ranger Chem PBT-201-G30 272 Flame Retarding FR PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishing grades (94V-0, V-2) exist, and electrical properties exhibited are the highest of any thermoplastic. Low water absorption is exhibited, and excellent electrical properties (CTI and GWIT) are retained over extended periods of usages, even with widely varied temperature and humidity conditions. The surface of molded products is smooth, and a low coefficient of friction is exhibited. As the amount of friction is low, PBT is suitable for use in application requiring friction and wear properties. The material is exceptionally reliable, with small in-use dimensional variation, and superior molding stability and dimensional precision. Long-term chemical resistance is exceptional, and at room temperature, there is almost no degradation in properties after. Both unreinforced and reinforced grades exhibit exceptional flowability, and excellent processability.Application: VCD drive frames Connectors Trimmers Switch buttons for gas-fired instantaneous water heaters Relay blocks Driers Rectifiers Outer handles Height sensor cases Door mirror stays Drive component housings Energy saving lamp.Information provided by Beijing Ranger Chemical Co.
Physical Properties Metric English Comments
Density 1.60 g/cc

@Temperature 23.0 °C
0.0578 lb/in³

@Temperature 73.4 °F
ASTM D792
Moisture Absorption at Equilibrium 0.050 %

@Temperature 23.0 °C,
Time 86400 sec
0.050 %

@Temperature 73.4 °F,
Time 24.0 hour
ASTM D570
Linear Mold Shrinkage 0.0040 - 0.0080 cm/cm
0.0040 - 0.0080 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 115 MPa
16700 psi
ASTM D638
Flexural Strength 180 MPa
26100 psi
ASTM D790
Flexural Modulus 8.00 GPa
1160 ksi
ASTM D790
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
ASTM D256
Izod Impact, Unnotched (ISO) 58.0 kJ/m²
27.6 ft-lb/in²
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 202 °C
396 °F
ASTM D648
Flammability, UL94 V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 1.30e+16 ohm-cm

@Thickness 2.00 mm
1.30e+16 ohm-cm

@Thickness 0.0787 in
ASTM D257
Dielectric Constant 3.2

@Frequency 50.0 Hz
3.2

@Frequency 50.0 Hz
ASTM D150
Dielectric Strength 20.0 kV/mm

@Thickness 2.00 mm
508 kV/in

@Thickness 0.0787 in
ASTM D149
Dielectric Loss Index 0.020

@Frequency 50.0 Hz
0.020

@Frequency 50.0 Hz
Tangent; ASTM D150
Processing Properties Metric English Comments
Nozzle Temperature 240 °C
464 °F
Melt Temperature 225 - 250 °C
437 - 482 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Injection Pressure 80.0 - 120 MPa
11600 - 17400 psi
Back Pressure 8.00 - 18.0 MPa
1160 - 2610 psi
Screw Speed <= 100 rpm
<= 100 rpm