Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 180 MPa | 26100 psi | ASTM D790 |
Premix Premi-Glas® 1200H-30 Fiberglass Reinforced Thermoset SMC Premi-Glas® 1200H-30 is a fiberglass reinforced thermoset sheet molding compound for general purpose and HVAC applications requiring thermal stability and stiffness.Key features and benefits are:Go.. |
|||
Flexural Strength | <= 180 MPa | <= 26100 psi | ISO 178 |
Polykemi AB POLYshine PBT D311 GF30 PBT, Glass-Fiber Reinforced, Modified Information provided by Polykemi AB |
|||
Flexural Strength | 180 MPa | 26100 psi | STN EN ISO 178 |
Plastcom SLOVASTER® B GF 30 FRL 4 Polybutylene Terephthalate, 30% Chemically Coupled Glass Fiber, Bromine Hydrocarbon Flame Retardant FeaturesPBT with the content of 30% chemically coupled glass fiber and flame retardant based on bromine hydrocarbons. Anisotropy of shrinkage enables injection moulding of round, cylindrical or oth.. |
|||
Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP DFL36ELH PC (Asia Pacific) LNP* Lubricomp* DFL36ELH is a compound based on Polycarbonate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Low Extractible. |
|||
Flexural Strength | 180 MPa | 26100 psi | |
Lehmann & Voss LUVOCOM® 1850-7783-1 PBT, with glass fiber, PTFE, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.High dimensionally stable prec.. |
|||
Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
Grupo Repol Dinalon® A1S25 G25PV0 25% Glass Reinforced, V-0 Rated (Phosphorous) Nylon 66 Mechanical properties are for dry as molded samples.Information provided by Grupo Repol. |
|||
Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
Grupo Repol Dinalon® B1S25 G30PV0 30% Glass Reinforced, V-0 Rated (Phosphorous) Nylon 6 Mechanical properties are for dry as molded samples.Information provided by Grupo Repol. |
|||
Flexural Strength | 180 MPa | 26100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP DF006HL PC LNP THERMOCOMP* DF006HL is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material include: Low Extractible, Healthcare. |
|||
Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
Vyncolit X655/1 Glass Fiber and Mineral Filled Novolac Phenolic Novolac resin based, glass fiber and mineral filled. High dimensional stability and excellent chemical resistance at high temperatures in hydraulic brake fluids. Used in particular in the ABS system.. |
|||
Flexural Strength | 180 MPa | 26100 psi | ISO 178-93 |
Wellman Wellamid® MRGF25/15 42H-N1/WE1705-N1 40% Mineral/Glass Fiber Reinforced Nylon 6 Description: Mineral/Glass Fiber Reinforced Nylon 6Information provided by Wellman. |
|||
Flexural Strength | 180 MPa | 26100 psi | ISO 178-93 |
Wellman Wellamid® MRGF30/10 42H-GY1 Nylon 6, 30% Mineral and 10% Glass Reinforced All information provided by Wellman Engineered Resins. |
|||
Flexural Strength | 180 MPa | 26100 psi | ASTM D638 |
A. Schulman POLYPUR™ FPU 1515 Thermoplastic Polyurethane Compound Information provided by A. Schulman. |
|||
Flexural Strength | 180 - 270 MPa | 26100 - 39200 psi | |
Alliance N-35SH Neodymium Iron Boron Magnetic Material |
|||
Flexural Strength | 180 - 270 MPa | 26100 - 39200 psi | |
Alliance N-35UH Neodymium Iron Boron Magnetic Material |
|||
Flexural Strength | 180 - 270 MPa | 26100 - 39200 psi | |
Alliance N-42M Neodymium Iron Boron Magnetic Material |
|||
Flexural Strength | 180 - 270 MPa | 26100 - 39200 psi | |
Alliance N-50 Neodymium Iron Boron Magnetic Material |
|||
Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
BASF Ultramid® B3EG6 LS BK 23189 30% Glass Filled PA6 (Conditioned) Information provided by BASF |
|||
Flexural Strength | 180 - 270 MPa | 26100 - 39200 psi | |
Alliance N-33UH Neodymium Iron Boron Magnetic Material |
|||
Flexural Strength | 180 - 270 MPa | 26100 - 39200 psi | |
Alliance N-38M Neodymium Iron Boron Magnetic Material |
|||
Flexural Strength | 180 - 270 MPa | 26100 - 39200 psi | |
Alliance N-48 Neodymium Iron Boron Magnetic Material |
|||
Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
BASF Ultradur® FRee B 4450 G5 LS 25% Glass Filled PBT Description: Is a PBT, injection-molding grade with 25% glass fibers for parts requiring enhanced fire resistance as well as increased tracking resistance (e.g. housings for electronics, plug-and-so.. |
|||
Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
Polyram PlusTek RA325G4 Nylon 66 for Injection Molding, 20% Glass-Fiber Reinforced, Self-Extinguishing, Halogen Free 20% Glass-fiber reinforced, self-extinguishing halogen free Nylon 66 for injection molding applications.Information provided by Polyram. |
|||
Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
Radici Radiflam® BRV300 AE Polybutylene Terephthalate PBT Self-extinguishing glass-fiber reinforced with halogenInformation provided by Radici group. |
|||
Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
Polyram RamSter PF321G4 PBT, 20% Glass Fiber, Flame Retardant 20% Glass fiber reinforce, flame retardant PBT for injection molding applications.Information provided by Polyram. |