- Polymer Property : Tensile Strength, Yield = 115 MPa
Polymer Property : Tensile Strength, Yield = 115 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 115 MPa | 16700 psi | 50 mm/min; ASTM D638 |
| Ovation Polymers Nima™ HL 30530 GF FR PET, 30% Glass Fiber PET – Flame Retardant 30% Short Glass Fiber Reinforced. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared according to ASTM s.. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics EXTEM UH1026 TPI Blend High heat amorphous TPI Blend, Chemical Resistant, High Flow, IR-Transparent |
|||
| Tensile Strength, Yield | 115 MPa @Temperature 23.0 °C |
16700 psi @Temperature 73.4 °F |
ISO 527 |
| Victrex® PEEK -HT™ G22 PolyEtherKetone, Unreinforced Product Description:High performance thermoplastic material, unreinforced PolyEtherKetone (PEK), semi crystalline, depth filtered granules for injection moulding, easy flow, FDA food contact complia.. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP IFL34 PA 6/12 (Asia Pacific) LNP* Lubricomp* IFL34 is a compound based on Nylon 6/12 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics ULTEM HU2100 PEI 10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). US FDA and European Food Contact approved. For medical devices and pharmaceutical applications.Healthcare management of change, biocom.. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics ULTEM HU2100 PEI (Asia Pacific) 10% Glass fiber filled, standard flow Polyetherimide (Tg 217C). US FDA and European Food Contact approved. For medical devices and pharmaceutical applications.Healthcare management of change, biocom.. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | ASTM D638 |
| Solvay Specialty Polymers PrimoSpire® PR-351 Polyphenylene, Self-Reinforced (SRP) PrimoSpire® PR-351 resin is a higher flow, injection molding grade of PrimoSpire® self-reinforced polyphenylene (SRP). PrimoSpire® SRP resin is an ultra-high performance amorphous, melt-pro.. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® 412 PBT (Europe-Africa-Middle East) VALOX 412 is 20% glass reinforced PBT injection moulding resin. Applications: Spotlights, appliance housings and handles. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® 8032U PBT+PET (Europe-Africa-Middle East) VALOX 8032U is a 30% glass fibre reinforced, UV stabilized PBT+PET blend with excellent surface finish. Applications: appliance housings, door handles, mirror brackets. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® 8032UX PBT+PET VALOX 8032UX is a 30% glass fibre reinforced, UV stabilized PBT+PET blend with excellent surface finish. This grade is VALOX 8032U with improved weathering resistance. Applications: appliance housin.. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® 8032UX PBT+PET (Asia Pacific) VALOX 8032UX is a 30% glass fibre reinforced, UV stabilized PBT+PET blend with excellent surface finish. This grade is VALOX 8032U with improved weathering resistance. Applications: appliance housin.. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® ENH4550 PBT (Asia Pacific) 25% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics Valox® ENH4550 PBT (Europe-Africa-Middle East) 25% GF reinforced, Non-Brominated & Non-Chlorinated Flame Retardant, PBT resin. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Valox® IQ8280SF PBT+PET Valox iQ8280SF resin is an environmentally responsible, low carbon footprint, and sustainable resin. Valox iQ8280SF resin offer Super High Flow characteristics combined with high modulus and excell.. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Valox® IQ8280SF PBT+PET (Europe-Africa-Middle East) Valox iQ8280SF resin is an environmentally responsible, low carbon footprint, and sustainable resin. Valox iQ8280SF resin offer Super High Flow characteristics combined with high modulus and excell.. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP THERMOCOMP RF003ES PA 66 LNP* THERMOCOMP* RF003ES is a Nylon 66 base resin containing 15% Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | SABIC - Japan Method |
| SABIC Innovative Plastics NORYL HM3020H PPE+PS (Asia Pacific) PPE+PS GF+MF 30% filled, FR V-1, high flow |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Ultem LTX931A PEI Blend (Europe-Africa-Middle East) Post-industrial recycle based, 30% glass fiber filled, high flow Polyetherimide blend. ECO Conforming.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | ISO 527-2 |
| Borealis Xmod™ GB305HP High Performance 35% Glass Fiber Reinforced Xmod GB305HP is reinforced with 35% chemically coupled glass fibers and based on a specific Polymer matrix material that is bringing excellent mechanical properties (biaxial impact behavior) as well.. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | ISO 527 |
| Polyram Polytron P40N03 Polypropylene, 40% Long Glass Fibers Is a chemically coupled 40% long glass fibers reinforced natural polypropylene, heat stabilized, for injection molding applications. These products have significantly improved impact performance ch.. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | ISO 527 |
| Eurostar Staramide RFM3353EM PA66/6, Glass/Mineral Fiber Reinforced, Injection Molding Starflam RFM3353EM is a Mineral Filled, Glass Fiber Reinforced Polyamide 66/ Polyamide 6 Injection Molding ResinInformation provided by Eurostar. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | 50 mm/min; ISO 527-1/-2 |
| BASF Ultramid® B3WGM 24 HP BK 23210 10/20% Glass/Mineral Filled PA6-1 (Conditioned) Description: 20% mineral-filled and 10% glass-fiber reinforced injection-molding grade with outstanding flowability for technical parts with medium rigidity and high dimensional stability, e.g. for.. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | ASTM D638 |
| Beijing Ranger Chem PBT-201-G25 211 Flame Retarding FR PBT Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin.. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | ASTM D638 |
| Beijing Ranger Chem PBT-201-G30 202 Environmental Protection Flame Retarding FR PBT Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin.. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® HFD4413 PC (Europe-Africa-Middle East) Lexan* HFD4413 is a 30% glass filled, injection moldable grade designed for high flow and superior surface appearance. Internal mold release. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP DFL28EG PC LNP* Lubricomp* DFL28EG is a compound based on Polycarbonate resin containing 40% Glass Fiber and 10% PTFE. Added features include: Internally Lubricated, Easy Molding. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP DFL369XF PC (Asia Pacific) LNP* Lubricomp* DFL369XF is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Retardant. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Noryl GFN1430V PPE+PS (Europe-Africa-Middle East) Noryl* GFN1430V PolyPhenylene Oxide (PPO*) + Polystyrene (PS) resin is a 30 % Glass Reinforced, injection moldable grade with improved hydrolytic stability. This grade has been developed for potable.. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | ISO 527-1/2 |
| Radici Radiflam® BRV300 AE Polybutylene Terephthalate PBT Self-extinguishing glass-fiber reinforced with halogenInformation provided by Radici group. |
|||
| Tensile Strength, Yield | 115 MPa | 16700 psi | 50mm/min; ISO 527 |
| BASF Ultramid® B3WG6 30% Glass Filled PA6 (Conditioned) Ultramid B3WG6 is a 30% glass fiber reinforced, heat stabilized injection molding PA6 grade. |
|||