BASF Ultramid® T 4381 LDS 10/25% Glass/Mineral Filled PA6/6T (Dry)

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced
Manufacturer	BASF
Trade Name	Ultramid®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Ultramid® T 4381 LDS 10/25% Glass/Mineral Filled PA6/6T (Dry).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Ultramid® T 4381 LDS is a semi-crystalline, partially aromatic high temperature polyamide (PA6/6T) for laser direct structuring (LPKFLDS®). As the material is reinforced with 10% fiberglass and 25% mineral filling, high-strength mechatronic plastic parts can be manufactured efficiently, quickly and flexibly with LDS. The innovative material offers a broad processing window for optimal results regarding: laser activation, metallization, adhesion of the conductors. Ultramid T 4381 LDS is based on Ultramid T and offers an ideal combination of high melting temperature, good processability and low water absorption. This specialty from BASF’s engineering plastics is already being used in electrical engineering and automotive construction, especially where high heat distortion temperature is required.Information provided by BASF

Physical Properties	Metric	English	Comments
Density	1.52 g/cc	0.0549 lb/in³	ISO 1183
Moisture Absorption at Equilibrium	0.80 - 1.2 %	0.80 - 1.2 %	50% RH; ISO 62
Viscosity Measurement	130	130	ISO 307

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	110 MPa	16000 psi	5mm/min; ISO 527-2
Tensile Strength, Yield	48.0 MPa	6960 psi	ISO 527
Elongation at Break	2.1 %	2.1 %	ISO 527-2
Elongation at Yield	5.0 %	5.0 %	ISO 527
Tensile Modulus	9.00 GPa	1310 ksi	ISO 527-2
Charpy Impact Unnotched	4.00 J/cm² @Temperature 23.0 °C	19.0 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eU

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	30.0 µm/m-°C	16.7 µin/in-°F	DIN 53152
CTE, linear, Transverse to Flow	50.0 µm/m-°C	27.8 µin/in-°F	DIN 53752
Melting Point	295 °C	563 °F	ISO 3146
Deflection Temperature at 0.46 MPa (66 psi)	265 °C	509 °F	ISO 75-2

Electrical Properties	Metric	English	Comments
Volume Resistivity	4.00e+12 ohm-cm	4.00e+12 ohm-cm	IEC 60093
Surface Resistance	>= 1.00e+16 ohm	>= 1.00e+16 ohm	ISO 60093
Dielectric Constant	4.4 @Frequency 1.00e+6 Hz	4.4 @Frequency 1.00e+6 Hz	IEC 60250
Dissipation Factor	0.015 @Frequency 1.00e+6 Hz	0.015 @Frequency 1.00e+6 Hz	IEC 60250

Descriptive Properties	Value	Comments
Color	Black
Commercial Status	Europe