BASF Ultramid® B3GM35 Q643 15/25% Glass/Mineral Filled PA6 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® B3GM35 Q643 15/25% Glass/Mineral Filled PA6 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultramid B3GM35 Q643 is a 40% combined glass-fiber and mineral reinforced injection molding PA6 grade.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| Water Absorption | 6.6 % | 6.6 % | ISO 62 |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 23°C/50% R.H.; ISO 62 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data; MD |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 123 MPa | 17800 psi | 0.2 in/min; ASTM Test |
| Tensile Strength, Ultimate | 123 MPa | 17800 psi | 5mm/min; ISO 527 |
| Elongation at Break | 2.6 % | 2.6 % | 0.2 in/min; ASTM Test |
| 2.7 % | 2.7 % | 5mm/min; ISO 527 | |
| Tensile Modulus | 7.96 GPa | 1150 ksi | 1mm/min; ISO 527 |
| Flexural Modulus | 7.50 GPa | 1090 ksi | ISO Data |
| Izod Impact, Notched | 0.400 J/cm @Temperature -40.0 °C |
0.749 ft-lb/in @Temperature -40.0 °F |
ASTM Test |
| 0.530 J/cm @Thickness 3.17 mm |
0.993 ft-lb/in @Thickness 0.125 in |
ASTM Test | |
| Izod Impact, Notched (ISO) | 4.80 kJ/m² | 2.28 ft-lb/in² | ISO Test |
| Charpy Impact, Notched | 0.410 J/cm² | 1.95 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10 K/min |
| 220 °C | 428 °F | ASTM Test | |
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C | 388 °F | ASTM Test |
| 199 °C | 390 °F | ISO 75 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding |