Armstrong C-4/W Epoxy Adhesive

Category Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive, Flexible
Manufacturer Armstrong Epoxy Adhesives; Resin Technology Group
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Armstrong C-4/W Epoxy Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
A low viscosity, clear amber, unfilled adhesive, recommended for use with activators D or W. C-4 with Activator W offers maximum versatility in that differing degrees of flexibility can be achieved by varying the mixing ratios within recommended limits. C-4 with Activator D is useful where an adhesive with a low mixed-viscosity is needed. It may also be used for fiberglass laminating or casting.Information provided by Ellsworth Adhesives.
Physical Properties Metric English Comments
Viscosity 10400 cP
10400 cP
Mixed
Mechanical Properties Metric English Comments
Hardness, Shore D 84
84
Tensile Strength, Ultimate 38.6 MPa
5600 psi
after optimum cure
Elongation at Break 12.5 %
12.5 %
Adhesive Bond Strength 36.2 MPa
5250 psi
Steel-Steel; after optimum cure
5.17 MPa

@Temperature 82.2 °C
750 psi

@Temperature 180 °F
Aluminum-Aluminum tensile shear
12.4 MPa

@Temperature 25.0 °C
1800 psi

@Temperature 77.0 °F
Aluminum-Aluminum tensile shear
16.9 MPa

@Temperature -54.4 °C
2450 psi

@Temperature -66.0 °F
Aluminum-Aluminum tensile shear
Thermal Properties Metric English Comments
CTE, linear 18.0 µm/m-°C

@Temperature 20.0 °C
10.0 µin/in-°F

@Temperature 68.0 °F
Glass Transition Temp, Tg 65.0 °C
149 °F
Processing Properties Metric English Comments
Processing Temperature 22.2 °C
72.0 °F
73.9 °C
165 °F
Optimum cure is 2 hr. @ 165°F
149 °C
300 °F
Fast cure is 5 min. @ 300°F
Pot Life <= 90.0 min

@Temperature 25.0 °C
<= 90.0 min

@Temperature 77.0 °F
100 g
Descriptive Properties Value Comments
Color Amber
Mix Ratio 1/1
By Weight