Armstrong A-2/W Epoxy Adhesive

Category	Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer	Armstrong Epoxy Adhesives; Resin Technology Group
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Armstrong A-2/W Epoxy Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

This off-white paste epoxy is a versatile adhesive systems. The choice of one of four recommended Activators (A, E, W or H-20) makes A-2 Adhesive an ideal choice for many applications. A-2 with Activators W or H-20 has a very low thermal expansion coefficient, especially important for bonding ceramics, porcelain, etc. A-2 with Activator A is qualified under Mil. Spec. MIL-A-47284 (MI).Information provided by Ellsworth Adhesives.

Physical Properties	Metric	English	Comments
Viscosity	130000 cP	130000 cP	Mixed

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	80	80
Tensile Strength, Ultimate	42.7 MPa	6200 psi	after optimum cure
Elongation at Break	3.1 %	3.1 %
Adhesive Bond Strength	39.0 MPa	5650 psi	Steel-Steel; after optimum cure
	8.27 MPa @Temperature 82.2 °C	1200 psi @Temperature 180 °F	Aluminum-Aluminum tensile shear
	20.0 MPa @Temperature -54.4 °C	2900 psi @Temperature -66.0 °F	Aluminum-Aluminum tensile shear
	37.6 MPa @Temperature 25.0 °C	5450 psi @Temperature 77.0 °F	Aluminum-Aluminum tensile shear

Thermal Properties	Metric	English	Comments
CTE, linear	86.0 µm/m-°C @Temperature 20.0 °C	47.8 µin/in-°F @Temperature 68.0 °F
Glass Transition Temp, Tg	60.0 °C	140 °F

Processing Properties	Metric	English	Comments
Processing Temperature	22.2 °C	72.0 °F
	93.3 °C	200 °F	Optimum cure is 30 min. @ 200°F
	149 °C	300 °F	Fast cure is 5 min. @ 300°F
Pot Life	<= 60.0 min @Temperature 25.0 °C	<= 60.0 min @Temperature 77.0 °F	100 g

Descriptive Properties	Value	Comments
Color	White
Mix Ratio	3/1	By Weight