ALM PA 860 White Nylon 11 SLS Prototyping Polymer
| Category | Polymer , Rapid Prototyping Polymer , Thermoplastic , Nylon , Nylon 11 |
| Manufacturer | ALM Advanced Laser Materials |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ALM PA 860 White Nylon 11 SLS Prototyping Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unfilled White PA 11 that is formulated for easy processing across all LS platforms. Tightly controlled particle distribution creates a smooth surface finish and excellent feature detail. Parts produced from PA 860 exhibit outstanding mechanical properties without the need to double scan. This material also exhibits very little out gassing, which decreases the potential for “fogging” on the laser window and IR sensors.Information provided by Advanced Laser Materials (ALM).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.620 g/cc | 0.0224 lb/in³ | ASTM D1895 |
| Density | 1.03 g/cc | 0.0372 lb/in³ | Sintered Part; ASTM D792 |
| Particle Size | 46 µm | 46 µm | Average D50; Laser Diffraction |
| 38 - 78 µm | 38 - 78 µm | Range (D10 to D90); Laser Diffraction | |
| Melt Flow | 26 g/10 min @Load 5.00 kg, Temperature 235 °C |
26 g/10 min @Load 11.0 lb, Temperature 455 °F |
3 min.; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 77 | 77 | |
| Tensile Strength at Break | 48.0 MPa | 6960 psi | XY direction; ASTM D638 |
| Tensile Strength, Ultimate | 42.0 MPa | 6090 psi | Z direction; ASTM D638 |
| Elongation at Break | 14 % | 14 % | Z direction; ASTM D638 |
| 51 % | 51 % | XY direction; ASTM D638 | |
| Tensile Modulus | 1.427 GPa | 207.0 ksi | Z direction; ASTM D638 |
| 1.475 GPa | 213.9 ksi | XY direction; ASTM D638 | |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 120 µm/m-°C @Temperature 0.000 - 50.0 °C |
66.7 µin/in-°F @Temperature 32.0 - 122 °F |
ASTM E831 |
| 342 µm/m-°C @Temperature 85.0 - 145 °C |
190 µin/in-°F @Temperature 185 - 293 °F |
ASTM E831 | |
| Melting Point | 201 °C | 394 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 184 °C | 363 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | ASTM D648 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | White |