A. Schulman ComAlloy Lubrilon® 631 Nylon 6/6, Graphite/Molybdenum Disulfide Filled

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, MoS2 Filled
Manufacturer	A. Schulman ComAlloy
Trade Name	Lubrilon®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	A. Schulman ComAlloy Lubrilon® 631 Nylon 6/6, Graphite/Molybdenum Disulfide Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulman product line.

Physical Properties	Metric	English	Comments
Density	1.24 g/cc	0.0448 lb/in³
Linear Mold Shrinkage	0.0080 cm/cm	0.0080 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	116	116	ASTM D785
Tensile Strength, Ultimate	81.0 MPa	11700 psi	ASTM D638
Elongation at Break	5.0 %	5.0 %	ASTM D638
Flexural Strength	130 MPa	18900 psi	ASTM D790
Flexural Modulus	4.10 GPa	595 ksi	ASTM D790
Izod Impact, Notched	0.320 J/cm	0.599 ft-lb/in	ASTM D256
Izod Impact, Unnotched	4.32 J/cm	8.09 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Melting Point	255 - 275 °C	491 - 527 °F
Deflection Temperature at 0.46 MPa (66 psi)	226 °C	439 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	102 °C	216 °F	ASTM D648

Processing Properties	Metric	English	Comments
Processing Temperature	290 °C	554 °F	Approximate middle barrel temperature.