Processing Properties | Metric | English | Comments |
---|---|---|---|
Cure Time | 300 min | 5.00 hour | work life |
Parker Chomerics CHO-SHIELD® 4966 Conductive Silicone Coating Conductive Silicone Coating. This is a conductive silver-filled silicone coating. This three-component system is capable of providing 60 dB of shielding effectiveness above 30 MHz. The coating utili.. |
|||
Cure Time | 300 - 360 min | 5.00 - 6.00 hour | 5 to 6 hours to send at 77°F. |
Fibre Glast 1100 Light-Weight High-Strength Patching/Filler Compound Product Features:Very Light Weight MaterialNon-Hazardous Product - Safe to UseEasily Sanded and Carved with Shop ToolsNegligible ShrinkageNon-Critical, 2 to 1 Ratio by Weight or by VolumeExcellent N.. |
|||
Cure Time | >= 300 min @Temperature 25.0 °C |
>= 5.00 hour @Temperature 77.0 °F |
|
Lord Adhesives Aeroglaze® 9743 Epoxy Primer/Tie-Coat Aeroglaze® 9743 is a two-part epoxy primer designed for use on aluminum, metal, and prepared composite surfaces. Aeroglaze 9743 primer/tie-coat can be applied to scuff-sanded urethane top coats a.. |
|||
Cure Time | >= 300 min @Temperature 25.0 °C |
>= 5.00 hour @Temperature 77.0 °F |
|
Lord Adhesives Aeroglaze® 9744 Epoxy Primer/Tie-Coat Aeroglaze® 9744 is a two-part epoxy primer designed for use on aluminum, metal, and prepared composite surfaces. Aeroglaze 9744 primer/tie-coat is applied to scuff-sanded urethane top coats and e.. |
|||
Cure Time | 300 min @Temperature 23.0 °C |
5.00 hour @Temperature 73.4 °F |
|
Shin-Etsu Silicones KE-1052D A/b Silicone, Gel RTV Information Provided by Shin-Etsu Silicones of America, Inc. |
|||
Cure Time | 300 min @Temperature 204 °C |
5.00 hour @Temperature 400 °F |
Recommended Post Cure Cycle |
Arlon 51576XC15A 0.015" Uncured/Cured Silicone Rubber with Fiberglass Substrate Design/Construction:Interleave: 3 mil PolyethyleneSide 2: Uncured Silicone RubberSubstrate: Style 7628 FiberglassSide 1: Cured Silicone RubberThis data represents typical values for the producti.. |
|||
Cure Time | 300 min | 5.00 hour | Tack-Free Time |
3M AC-251 Black Class B-1 Aerospace Sealant 3M Aerospace Sealant AC-251 Black Class B are two-part, quick curing, polysulfide based canopy and windshield sealants. These products are formulated for sealing acrylic, glass, and polycarbonate ai.. |
|||
Cure Time | 300 min | 5.00 hour | Tack-Free Time |
3M AC-350 Class A-1 Aerospace Sealant 3M Aerospace Sealant AC-350 Class A are fast-cure, intermediate density two-component, manganese dioxide cure, brushable, polysulfide fuel tank and fuselage sealants. 3M AC-350 Class A Sealants have.. |
|||
Cure Time | 300 - 360 min | 5.00 - 6.00 hour | |
3M AC-770 Class B-1 Aerospace Sealant 3M Aerospace Sealant AC-770 Class B are fast cure, low density two-component, manganese dioxide cure, polysulfide fuselage sealants. 3M AC-770 Class B Sealants have outstanding resistance to aviatio.. |
|||
Cure Time | 300 - 360 min | 5.00 - 6.00 hour | Full Hardness |
3M Scotchkote™ 165CS Urethane Sealer Scotchkote Urethane Sealer 165CS has been specifically developed as a low viscosity primer/sealer for concrete and cementitious surfaces prior to application of other Scotchkote urethane systems.Pro.. |
|||
Cure Time | 300 min | 5.00 hour | Touch Dry |
3M Scotchkote™ FB 857 Urethane Floor Coating Scotchkote Urethane Floor Coating FB 857 has been specifically developed as a 100% solids protection system with a degree of flexibility for application to concrete and asphalt floor surfaces.Produc.. |
|||
Cure Time | 300 - 420 min | 5.00 - 7.00 hour | 2-4 hrs at 200°F; 3 hrs at 250°F |
Aremco Ceramacast™ 575-N High Temperature Potting & Casting Material Alumina Fine grain castable for potting and producing small tools. |
|||
Cure Time | 300 - 420 min | 5.00 - 7.00 hour | 2-4 hrs at 200°F; 3 hrs at 250°F |
Aremco Ceramacast™ 576-N High Temperature Potting & Casting Alumina Medium grain castable ceramic for large high temperature potting and tooling. Aremco offers a range of ceramic-based materials used for the assembly of high temperature, high power electrical devic.. |
|||
Cure Time | 300 min | 5.00 hour | 2 hrs at 200°F; 3 hrs at 250°F |
Aremco Ceramacast™ 584 High Temperature Potting & Casting Material Magnesia Two-part, quick-set ceramic for small parts. |
|||
Cure Time | 300 - 420 min | 5.00 - 7.00 hour | 2-4 hrs at 200°F; 3 hrs at 250°F |
Aremco Ceramacast™ 645-N High Temperature Potting & Casting Material Silica Castable ceramic with low thermal conductivity. |
|||
Cure Time | 300 - 420 min | 5.00 - 7.00 hour | 2-4 hrs at 200°F; 3 hrs at 250°F |
Aremco Ceramacast™ 646-N High Temperature Potting & Casting Material Zirconia Castable ceramic with high dielectric and physical strength. |
|||
Cure Time | 300 - 420 min | 5.00 - 7.00 hour | 2-4 hrs at 200°F; 3 hrs at 250°F |
Aremco Ceramacast™ 673-N High Temperature Potting & Casting Material Silicon Carbide Single-part castable ceramic exhibiting high strength and thermal conductivity. |
|||
Cure Time | 300 - 420 min | 5.00 - 7.00 hour | 2-4 hrs at 200°F; 3 hrs at 250°F |
Aremco Ceramacast™ 675 High Temperature Potting & Casting Material Aluminum Nitride Fine grain aluminum nitride castable with high thermal conductivity |
|||
Cure Time | 300 - 420 min | 5.00 - 7.00 hour | 2-4 hrs at 200°F; 3 hrs at 250°F |
Aremco Ceramacast™ 675-N High Temperature Potting & Casting Material Aluminum Nitride Fine grain aluminum nitride castable with high thermal conductivity. |
|||
Cure Time | 300 - 420 min | 5.00 - 7.00 hour | 2-4 hrs at 200°F; 3 hrs at 250°F |
Aremco Ceramacast™ 900 High Temperature Potting & Casting Material Zirconia Silicate High Density, high strength molding compound. |
|||
Cure Time | 300 min | 5.00 hour | Time to Handling Strength |
3M Scotch-Weld™ LSB60 Toughened Epoxy Adhesives 3M™ Scotch-Weld™ Toughened Epoxy Adhesive LBS60 is a high performance, two-part, toughened epoxy adhesives offering outstanding shear adhesion and very high levels of durability with a choice of f.. |
|||
Cure Time | 300 min | 5.00 hour | Time to Handling Strength |
3M Scotch-Weld™ LSB60NS Toughened Epoxy Adhesives 3M™ Scotch-Weld™ Toughened Epoxy Adhesive LBS60NS is a high performance, two-part, toughened epoxy adhesives offering outstanding shear adhesion and very high levels of durability with a choice of.. |
|||
Cure Time | 300 - 420 min | 5.00 - 7.00 hour | 2-4 hrs Air Set; 3 hrs at 200°F |
Aremco Pyro-Putty™ 2500 High Temperature Ceramic-Metallic Putty, Iron Oxide Filled Ceramic and Black Iron Oxide-Filled, One-Part, Water Based Paste.For Applications to 1/4" Thick.Repairs Cast Iron, and Steel Parts to 1600°F |