Premix Thermoplastics PRE-ELEC® PA 1409 Conductive Thermoplastic Compound

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer Premix Thermoplastics Inc.
Trade Name PRE-ELEC®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Premix Thermoplastics PRE-ELEC® PA 1409 Conductive Thermoplastic Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PRE-ELEC® PA 1409 is a conductive thermoplastic compound based on polyamide 6. Conductivity is achieved by using conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® PA 1409 has an excellent balance of mechanical properties and is easy to injection mould.Applications: Injection moulded housings, boxes and technical parts. PRE-ELEC® PA 1409 is well suited for applications where the good mechanical properties of polyamide are required. Processing: PRE-ELEC® PA 1409 compound can be processed in the injection moulding machines using normal processing conditions as with polyamide.Test Specimen: 10[mm] wide moulded rodInformation from Premix OY
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
Thickness 102 microns
4.00 mil
Linear Mold Shrinkage 0.016 - 0.022 cm/cm
0.016 - 0.022 in/in
ISO 294-4
Melt Flow 8.5 g/10 min

@Load 5.00 kg,
Temperature 275 °C
8.5 g/10 min

@Load 11.0 lb,
Temperature 527 °F
ISO 1133
43 g/10 min

@Load 10.0 kg,
Temperature 275 °C
43 g/10 min

@Load 22.0 lb,
Temperature 527 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 85
85
ISO 868
Tensile Strength 58.0 MPa
8410 psi
ISO 527
Tensile Strength, Yield 59.0 MPa
8560 psi
ISO 527
Elongation at Break 29 %
29 %
ISO 527
Elongation at Yield 8.0 %
8.0 %
ISO 527
Flexural Modulus 2.90 GPa
421 ksi
ISO 178
Izod Impact, Notched (ISO) 4.00 kJ/m²

@Thickness 4.00 mm,
Temperature -20.0 °C
1.90 ft-lb/in²

@Thickness 0.157 in,
Temperature -4.00 °F
ISO 180
11.0 kJ/m²

@Thickness 4.00 mm,
Temperature 23.0 °C
5.23 ft-lb/in²

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Izod Impact, Unnotched (ISO) 51.0 kJ/m²

@Thickness 4.00 mm,
Temperature -20.0 °C
24.3 ft-lb/in²

@Thickness 0.157 in,
Temperature -4.00 °F
ISO 180
NB

@Thickness 4.00 mm,
Temperature 23.0 °C
NB

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Charpy Impact Unnotched NB

@Thickness 102 mm,
Temperature 23.0 °C
NB

@Thickness 4.00 in,
Temperature 73.4 °F
ISO 179
NB

@Thickness 102 mm,
Temperature -20.0 °C
NB

@Thickness 4.00 in,
Temperature -4.00 °F
ISO 179
Charpy Impact, Notched 0.700 J/cm²

@Thickness 102 mm,
Temperature -20.0 °C
3.33 ft-lb/in²

@Thickness 4.00 in,
Temperature -4.00 °F
ISO 179
1.00 J/cm²

@Thickness 102 mm,
Temperature 23.0 °C
4.76 ft-lb/in²

@Thickness 4.00 in,
Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 168 °C
334 °F
75/Method Bf
Deflection Temperature at 1.8 MPa (264 psi) 70.0 °C
158 °F
75/Method Af
Vicat Softening Point 190 °C
374 °F
ISO 306/B50
218 °C
424 °F
ISO 306/A50
Electrical Properties Metric English Comments
Volume Resistivity <= 1000 ohm-cm
<= 1000 ohm-cm
ISO D-257
Surface Resistance <= 1e+05
<= 1e+05
ISO IEC 61340-5-1
Processing Properties Metric English Comments
Melt Temperature 220 - 280 °C
428 - 536 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 80.0 °C
176 °F
Pre-drying
Dry Time 2 - 4 hour
2 - 4 hour
Injection Pressure 60.0 - 80.0 MPa
8700 - 11600 psi
Shelf Life 12.0 Month
12.0 Month
Normal Storing Conditions
Descriptive Properties Value Comments
Injection Speed Moderate