Polymer Resources NY6-IM1-[color]-H Nylon 6, Impact Modified, Heat Stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Heat Stabilized , Nylon 6, Impact Grade |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources NY6-IM1-[color]-H Nylon 6, Impact Modified, Heat Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6, Impact Modified, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.016 - 0.020 cm/cm | 0.016 - 0.020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Flexural Strength | 75.8 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm @Temperature 22.8 °C |
3.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Gardner Impact | 36.2 J | 26.7 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 168 °C | 335 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.8 °C | 145 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0626 in |
|
| HB @Thickness 3.17 mm |
HB @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 221 - 246 °C | 430 - 475 °F | |
| Middle Barrel Temperature | 238 - 254 °C | 460 - 490 °F | |
| Front Barrel Temperature | 243 - 260 °C | 470 - 500 °F | |
| Melt Temperature | 238 - 268 °C | 460 - 515 °F | |
| Mold Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Drying Temperature | 73.9 - 85.0 °C | 165 - 185 °F | |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0003 |
Users viewing this material also viewed the following:
- Ritelok HP45 High Pressure Sealant
- Nilit FRIANYL A63 GV25 Nylon 6.6 for injection molding, 25% glass fiber reinforced
- Loxim 831 02T HB Polypropylene Compound, 30% Talc Filled, Flame Retardant
- SABIC Innovative Plastics NORYL WCV072 PPE+PP
- DuPont Elvaloy® 4924 Ethylene/Vinyl Acetate/Carbon Monoxide Copolymer
- E-Polymers TEKAMID® TB120L Lubricated PA6, DAM
- 3M AC-350 Class B-2 Aerospace Sealant
- 3M FM14K Indoor UL Recognized Computer Imprintable Clear Polyester Label Product
- 3M 9576R Splicing Tape
- Potters Industries A-Series Z-CEL® 8054 White Synthetic Sodium Aluminosilicate Microsphere
Copyright © lookpolymers.com All Rights Reserved