Aardvark Polymers AARTEL® 2100UV Acetal Homopolymer Rotational Molding Resin

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced, Impact Grade
Manufacturer Gehrig & Associates
Trade Name AARTEL®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Aardvark Polymers AARTEL® 2100UV Acetal Homopolymer Rotational Molding Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Aartel 2100UV is a natural acetal homopolymer with UV stabilizers.Aartel 2100UV is a medium viscosity resin with excellent flow characteristics.Aartel 2100UV is available in natural white and may be painted, printed, or plated.Aartel 2100UV may be compounded and dry colored.Aartel 2100UV offers exceptional resistance to aggressive chemicals and fuels.Aartel 2100UV has a fuel permeation rate of 1.2gr-mm/m2-day.
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
Water Absorption 0.50 %
0.50 %
24 hour immersion
Moisture Absorption at Equilibrium 0.17 %
0.17 %
50% RH
Water Absorption at Saturation 1.2 %
1.2 %
Linear Mold Shrinkage, Flow 0.020 cm/cm

@Thickness 2.00 mm
0.020 in/in

@Thickness 0.0787 in
Linear Mold Shrinkage, Transverse 0.019 cm/cm

@Thickness 2.00 mm
0.019 in/in

@Thickness 0.0787 in
Mechanical Properties Metric English Comments
Hardness, Rockwell M 92
92
Hardness, Rockwell R 120
120
Test 1
120
120
Test 2
Tensile Strength, Ultimate 67.0 MPa
9720 psi
5 mm/min (0.2 in/min)
Tensile Strength, Yield 67.0 MPa
9720 psi
5 mm/min (0.2 in/min)
70.0 MPa
10200 psi
Elongation at Break 30 %
30 %
Nominal
45 %
45 %
5 mm/min (0.2 in/min)
Elongation at Yield 13 %
13 %
5 mm/min (0.2 in/min)
17 %
17 %
Tensile Modulus 3.10 GPa
450 ksi
3.23 GPa
468 ksi
5 mm/min (0.2 in/min)
Flexural Modulus 3.00 GPa
435 ksi
3.05 GPa
442 ksi
Izod Impact, Unnotched 0.800 J/cm
1.50 ft-lb/in
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
8.00 kJ/m²

@Temperature -40.0 °C
3.81 ft-lb/in²

@Temperature -40.0 °F
Charpy Impact Unnotched 26.0 J/cm²
124 ft-lb/in²
26.0 J/cm²

@Temperature -30.0 °C
124 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
0.800 J/cm²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
Impact 1870
1870
J/m; Unnotched
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 120 µm/m-°C

@Temperature 23.0 - 55.0 °C
66.7 µin/in-°F

@Temperature 73.4 - 131 °F
121 µm/m-°C

@Temperature 23.0 - 55.0 °C
67.2 µin/in-°F

@Temperature 73.4 - 131 °F
CTE, linear, Transverse to Flow 120 µm/m-°C

@Temperature 23.0 - 55.0 °C
66.7 µin/in-°F

@Temperature 73.4 - 131 °F
120 µm/m-°C

@Temperature 23.0 - 55.0 °C
66.7 µin/in-°F

@Temperature 73.4 - 131 °F
Melting Point 178 °C
352 °F
10°C/min
178 °C
352 °F
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
320 °F
168 °C
334 °F
Unannealed
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
104 °C
219 °F
Unannealed
UL RTI, Electrical 50.0 °C

@Thickness 1.50 mm
122 °F

@Thickness 0.0591 in
50.0 °C

@Thickness 3.00 mm
122 °F

@Thickness 0.118 in
UL RTI, Mechanical with Impact 50.0 °C

@Thickness 1.50 mm
122 °F

@Thickness 0.0591 in
50.0 °C

@Thickness 3.00 mm
122 °F

@Thickness 0.118 in
UL RTI, Mechanical without Impact 50.0 °C

@Thickness 1.50 mm
122 °F

@Thickness 0.0591 in
50.0 °C

@Thickness 3.00 mm
122 °F

@Thickness 0.118 in
Flammability, UL94 HB

@Thickness 0.840 mm
HB

@Thickness 0.0331 in
Test 1
HB

@Thickness 0.840 mm
HB

@Thickness 0.0331 in
Test 2
HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Test 1
HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Test 2
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Test 1
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Test 2
Oxygen Index 22 %
22 %
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+11 ohm-cm
1.00e+11 ohm-cm
Test 1
1.00e+14 ohm-cm
1.00e+14 ohm-cm
Test 2
Surface Resistance 6.00e+14 ohm
6.00e+14 ohm
Dielectric Constant 3.4
3.4
3.5

@Frequency 100 Hz
3.5

@Frequency 100 Hz
3.8

@Frequency 1e+6 Hz
3.8

@Frequency 1e+6 Hz
Dissipation Factor 0.0060

@Frequency 1e+6 Hz
0.0060

@Frequency 1e+6 Hz
0.018

@Frequency 100 Hz
0.018

@Frequency 100 Hz
Comparative Tracking Index 600 V
600 V