SABIC Innovative Plastics Ultem DH1004F PEI (Asia Pacific)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Ultem DH1004F PEI (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High Temperature, Transparent, Polyetherimide Blend with Improved Ductility and Enhanced Hydrostability. US FDA and EU Food Contact compliant.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.28 g/cc
1.28 g/cc
ASTM D 792
Density 1.28 g/cc
0.0462 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 10 g/10 min

@Load 6.60 kg,
Temperature 337 °C
10 g/10 min

@Load 14.6 lb,
Temperature 639 °F
ASTM D 1238
14 g/10 min

@Load 5.00 kg,
Temperature 360 °C
14 g/10 min

@Load 11.0 lb,
Temperature 680 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 80.0 MPa
11600 psi
50 mm/min; ISO 527
90.0 MPa
13100 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 95.0 MPa
13800 psi
Type I, 5 mm/min; ASTM D 638
97.0 MPa
14100 psi
50 mm/min; ISO 527
Elongation at Break 80 %
80 %
50 mm/min; ISO 527
85 %
85 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 7.0 %
7.0 %
Type I, 5 mm/min; ASTM D 638
7.0 %
7.0 %
50 mm/min; ISO 527
Tensile Modulus 2.90 GPa
421 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 136 MPa
19700 psi
2 mm/min; ISO 178
140 MPa
20300 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.80 GPa
406 ksi
2 mm/min; ISO 178
3.00 GPa
435 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.700 J/cm

@Temperature 23.0 °C
1.31 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
33.0 J/cm

@Thickness 3.20 mm
61.8 ft-lb/in

@Thickness 0.126 in
reverse notched; ASTM D 256
Izod Impact, Notched (ISO) 6.00 kJ/m²

@Temperature 23.0 °C
2.86 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
6.00 kJ/m²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
80*10*4; ISO 180/1U
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
80*10*4; ISO 180/1U
Charpy Impact, Notched 1.10 J/cm²

@Temperature 23.0 °C
5.23 ft-lb/in²

@Temperature 73.4 °F
ISO 179/2C
Impact Test 88.0 J

@Temperature 23.0 °C
64.9 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
88.0 J

@Temperature -20.0 °C
64.9 ft-lb

@Temperature -4.00 °F
Instrumented Impact Total Energy; ASTM D 3763
99.0 J

@Temperature 0.000 °C
73.0 ft-lb

@Temperature 32.0 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 50.0 µm/m-°C

@Temperature 23.0 - 150 °C
27.8 µin/in-°F

@Temperature 73.4 - 302 °F
ISO 11359-2
56.0 µm/m-°C

@Temperature -20.0 - 150 °C
31.1 µin/in-°F

@Temperature -4.00 - 302 °F
ASTM E 831
CTE, linear, Transverse to Flow 50.0 µm/m-°C

@Temperature 23.0 - 150 °C
27.8 µin/in-°F

@Temperature 73.4 - 302 °F
ISO 11359-2
55.0 µm/m-°C

@Temperature -20.0 - 150 °C
30.6 µin/in-°F

@Temperature -4.00 - 302 °F
ASTM E 831
Thermal Conductivity 0.190 W/m-K
1.32 BTU-in/hr-ft²-°F
ASTM C 177
Deflection Temperature at 0.46 MPa (66 psi) 205 °C
401 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
214 °C

@Thickness 6.40 mm
417 °F

@Thickness 0.252 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 190 °C
374 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
204 °C

@Thickness 6.40 mm
399 °F

@Thickness 0.252 in
unannealed; ASTM D 648
Vicat Softening Point 212 °C
414 °F
Rate B/50; ISO 306
212 °C
414 °F
Rate B/120; ISO 306
219 °C
426 °F
Rate A/50; ISO 306
Flammability, UL94 V-0

@Thickness 0.750 mm
V-0

@Thickness 0.0295 in
UL 94
NBS Smoke Density 0.70

@Time 240 sec
0.70

@Time 0.0667 hour
Flaming, Ds; ASTM E 662
Oxygen Index 46 %
46 %
LOI; ASTM D 2863
Optical Properties Metric English Comments
Transmission, Visible 90 %
90 %
transparent; thickness not quantified
Descriptive Properties Value Comments
Instrumented Impact Ductility, 0°C, % 100
ASTM D 3763
Instrumented Impact Ductility, -20°C, % 90
ASTM D 3763
Instrumented Impact Ductility, 23°C, % 100
ASTM D 3763