- Polycarbonate, 10% Glass Filled
- Polyram RamTough RZ300G2 Polycarbonate, 10% Glass Fiber
Polyram RamTough RZ300G2 Polycarbonate, 10% Glass Fiber
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamTough RZ300G2 Polycarbonate, 10% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
10% Glass fiber reinforced polycarbonate for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 0.29 % | 0.29 % | ISO 62 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ISO 2577 |
| Melt Flow | 12 g/10 min @Load 1.20 kg, Temperature 300 °C |
12 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527 |
| Elongation at Break | 15 % | 15 % | ISO 527 |
| Tensile Modulus | 3.12 GPa | 453 ksi | ISO 527 |
| Flexural Strength | 95.0 MPa | 13800 psi | ISO 178 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 7.50 kJ/m² | 3.57 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.220 W/m-K | 1.53 BTU-in/hr-ft²-°F | DIN 52612 |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ISO 75 |
| Flammability, UL94 | V-2 @Thickness 3.00 mm |
V-2 @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 3.2 | 3.2 | IEC 60250 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- Intercontinental Polymers 132 PET Polymer Type - Semi-Dull, Flame Retardant, Polyester Pellets
- Saint-Gobain CHR® M56 Polyester Film Backing Natural Rubber Adhesive Pressure Sensitive Tape
- A. Schulman SCHULAMID® 6 GF35 35% Glass Fiber Reinforced Nylon 6
- DuPont Elvax® 240W Ethylene Vinyl Acetate
- Total PPC 4660 Polypropylene, Heterophasic Copolymer
- ELASTO UK Mediprene™ 500600M TPE, Medical Applications, 60A Hardness
- Dymax 3072P Fast Shallow Potting Compound and Sealant
- BASF Luranyl® KR 2401 Polyphenylene Ether + Styrene-Butadiene Blend, Impact Grade
Copyright © lookpolymers.com All Rights Reserved