Polymer Property : Flexural Modulus = 1.38 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	1.38 GPa	201 ksi	ASTM D790
PolyMirae Moplen EP340K Sheet and Thermoforming Grade Polypropylene Moplen RP340K is the polypropylene random copolymer polymer manufactured by PMC under the license of BASELL using the Spheripol process. Moplen RP340K is a random copolymer particularly suitable for..
Flexural Modulus	1.38 GPa	200 ksi	Tangent; ASTM D790
RheTech Products HP522-473 15% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, ZU5A Dark Graphite Applications: ConsolesClose out panelInjection molding conditions reported in table.Information provided by RheTech Products.
Flexural Modulus	1.38 - 2.76 GPa	200 - 400 ksi	ASTM D790
Alcoa KAMA 3210 Hi-Gloss Coextruded High Impact Polystyrene (discontinued **) CapabilitiesGauge: .007” to .060” (178 to 1524µm)Width: 12” to 62” (304 to 1575mm)Core Size: 6” standard cores, 3” and 8” availableRoll O.D.: 29” standard, up to 40” availableSilicone coat..
Flexural Modulus	1.38 - 26.3 GPa	200 - 3810 ksi	Average value: 9.59 GPa Grade Count:124
Overview of materials for Polycarbonate, Carbon Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Carbon Fiber Reinforced". Each property range of values reported is minimum and maximum v..
Flexural Modulus	1.38 GPa	200 ksi	ASTM D790
I. Stern IS-35955 High Density Polyethylene, Blow Molding Grade Features:IS-35955 is designed for applications requiring excellent stiffness and stress crack resistance properties.Meets all requirements of the U. S. Food and Drug Administration as specified in 2..
Flexural Modulus	1.38 GPa	200 ksi	1% Secant, 0.05 in/min; ASTM D790
LyondellBasell Pro-faxâ„¢ PH350 Polypropylene Homopolymer Description: Pro-faxâ„¢ PH350 general purpose polypropylene homopolymer resin is available as natural flake. Flake form resin is well suited for mixing with pigments and other additives to make p..
Flexural Modulus	1.38 GPa	200 ksi	ASTM D790B
Ineos R12C-01 Polypropylene Random Copolymer Grade R12C-01 is a high clarity, antistatic polypropylene copolymer for injection molding and stretch blow molding applications. This material meets the requirements of the U.S. Food and Drug Admini..
Flexural Modulus	1.38 GPa	200 ksi	ASTM D790
Techmer ES HiFillÂ® HDPE TM30 30% Talc Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Talc Filler, 30% Filler by WeightInformation provided by TP Composites, Inc.
Flexural Modulus	1.38 GPa	200 ksi	ASTM D790
Spartech SP-3810 TPO/TPE Polyolefin Sheet Description: Polyolefin SheetInformation provided by Spartech.
Flexural Modulus	1.38 GPa	200 ksi	ASTM D790
A. Schulman PP 3488-01 Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3488-01 is a specially formulated homopolymer polypropylene designed for large appliance injection molding. This material has excellent chemical resistance in addition t..
Flexural Modulus	1.38 GPa	200 ksi	ASTM D790
Chase Plastics CP Pryme® NN100STL (DAM) Nylon 66, Super Toughened, Internally Lubricated Information provided by Chase Plastics.
Flexural Modulus	1.38 GPa	200 ksi	ASTM D790
A. Schulman PP 3490-01G Polypropylene Homopolymer Polypropylene DescriptionPolypropylene PP 3490-01G Natural is a homopolymer for extrusion and compounding applications. This material can also be used as a carrier resin for color concentrates. ApplicationPP 349..
Flexural Modulus	1.38 GPa	200 ksi	ASTM D790
A. Schulman PP 3449-01 Polypropylene Copolymer Polypropylene DescriptionPolypropylene PP 3449-01 is a new generation copolymer polypropylene utilizing unique catalyst technology. Combining an excellent balance of high stiffness and impact. This product inc..
Flexural Modulus	1.38 GPa	200 ksi	ASTM D 790
Total 5502 BZ HDPE injection blow molding Applications: Cosmetics and toiletries, pharmaceuticals, specialty containers, food packagingInformation provided provided by Total Petrochemicals.Total Petrochemicals acquired former Fina and Atof..
Flexural Modulus	1.38 GPa	200 ksi	ASTM D790
Total PPH 3480Z Polypropylene, Extrusion Grade Homopolymer Profile Extrusion GradeProcess Stability --FINA 3480Z is formulated specifically to give excellent process stability in high profile extrusion.High Purity - Low catalyst residues in FINA..
Flexural Modulus	1.38 GPa	200 ksi	ASTM D790
A. Schulman POLYTROPE™ TPP 620 Olefinic Elastomer DescriptionPolytrope TPP 620is an olefinic elastomer developed to exhibit very low thermal expansion, high DOI on painted parts with good low temperature impact properties. ApplicationTPP 620 is des..
Flexural Modulus	1.38 GPa	200 ksi	ASTM D790
A. Schulman PP 3449-01 Polypropylene Copolymer Polypropylene DescriptionPolypropylene PP 3449-01 is a new generation copolymer polypropylene utilizing unique catalyst technology. Combining an excellent balance of high stiffness and impact. This product inc..
Flexural Modulus	1.38 GPa	200 ksi	ASTM D790
Total PPC 4820WZ Polypropylene, Impact Copolymer TOTAL Petrochemicals Polypropylene 4820WZ is a nucleated impact copolymer with a Melt Flow index of 35 g/10 min.TOTAL Polypropylene 4820WZ is characterized by improved stiffness, creep resistance, h..
Flexural Modulus	1.38 GPa	200 ksi	ASTM D790
A. Schulman PP 3449-01 Polypropylene Copolymer Polypropylene DescriptionPolypropylene PP 3449-01 is a new generation copolymer polypropylene utilizing unique catalyst technology. Combining an excellent balance of high stiffness and impact. This product inc..
Flexural Modulus	1.38 GPa	200 ksi	0.05 in/min, 1% secant; ASTM D-790A
Braskem TI4350P Impact Copolymer Polypropylene Description: Good balance of stiffness and impact strength, excellent organoleptic properties.Applications: Suggested uses include compounding, thin-walled injection molding.Process: Injection Moldi..
Flexural Modulus	1.38 GPa	200 ksi	ASTM D790
Aaron Industries AAROLENE® ARPP H 200-1 PP Black Polypropylene Homopolymer Compounded Resin AAROLENE® ARPP 200 Series Polypropylene Compounded ResinFeatures: A pre-colored, black homopolymer polypropylene resin specifically designed for all injection molding applications.High Flow
Flexural Modulus	1.38 GPa	200 ksi	ASTM D 790
Total Finathene® RS 528 HDPE blow molding (discontinued **) Applications: Bleach and detergents, industrial chemicals, industrial parts, cosmetic bottles, food packaging.Information provided provided by Total Petrochemicals.Total Petrochemicals includes form..
Flexural Modulus	1.38 - 11.0 GPa	200 - 1600 ksi	Average value: 3.70 GPa Grade Count:107
Overview of materials for Nylon 66, PTFE Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, PTFE Filled". Each property range of values reported is minimum and maximum values of appropri..
Flexural Modulus	1.38 GPa	200 ksi	0.05 in/min; 1% secant; Procedure A; ASTM D790
Phillips 66 COPYLENE® CH016 Polypropylene, Homopolymer, BOPP COPYLENE™ CH016 is a polypropylene homopolymer resin designed for BOPP (biaxially oriented polypropylene) film extrusion applications. Applications: Bags & Pouches; Raffia/Tapes/Strapping; Peelable..
Flexural Modulus	1.38 - 2.76 GPa	200 - 400 ksi	ASTM D790
Alcoa KAMA 3200 Prime High Impact Polystyrene (discontinued **) CapabilitiesGauge: .007” to .060” (178 to 1524µm)Width: 12” to 62” (304 to 1575mm)Core Size: 6” standard cores, 3” and 8” availableRoll O.D.: 29” standard, up to 40” availableSilicone trea..
Flexural Modulus	1.38 GPa	200 ksi	ASTM D790A
Ineos H05H-01 Polypropylene Homopolymer Grade H05H-01 is a homopolymer polypropylene for injection molding applications. It is an excellent long-term heat aging grade and offers superior extraction resistance in hot aqueous solutions. T..
Flexural Modulus	1.38 GPa	200 ksi	1.3mm per min, 1% secant; ASTM D790
Formosa Plastics Formolene® 1102KR Cast Film Polypropylene HomopolymerApplications: Cast film applications such as slit tape fabric stock and cordage.Formolene 1102KR is a highly isotactic polypropylene homopolymer designed primarily for cast film applicati..