Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | >= 500 MPa | >= 72500 psi | EN 10002-1 |
Outokumpu 4541 Cr-Ni Austenitic Stainless Steel Good corrosion resistance and weldable. Resistant to sensitization.Applications: Welded screensFurnace beltsCatalytic converter meshAvailable in hot rolled plate (Quarto), hot rolled strip/sheet (C.. |
|||
Tensile Strength, Ultimate | 500 - 540 MPa | 72500 - 78300 psi | after heat treatment |
PEAK Werkstoff DISPAL S691 Aluminum Alloy, AlCu5Ti High stiffness and elongation at ruptureInformation provided by PEAK Werkstoff GmbH |
|||
Tensile Strength, Ultimate | 500 MPa | 72500 psi | |
Haynes Hastelloy® W alloy as a weld filler, base metal Carbon steel 12.7 mm plate weldments Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemica.. |
|||
Tensile Strength, Ultimate | 500 MPa @Temperature 870 °C |
72500 psi @Temperature 1600 °F |
|
Haynes 242® alloy, bar and rings, annealed and aged Age-hardenable, high ductility in the aged condition, lower thermal expansion than most alloys, very good oxidation resistance up to 815°C, excellent low cycle fatigue properties, very good therm.. |
|||
Tensile Strength, Ultimate | 500 MPa @Temperature 550 °C |
72500 psi @Temperature 1020 °F |
Annealed prior to test |
Special Metals BRIGHTRAY® Alloy 35 Electrical Resistance Alloy A nickel-iron-chromium electrical-resistance alloy for use at operating temperatures up to 1920°F (1050°C). It is similar to BRIGHTRAY alloy F but with rare-earth additions for greater resist.. |
|||
Tensile Strength, Ultimate | 500 MPa @Temperature 550 °C |
72500 psi @Temperature 1020 °F |
Annealed prior to test |
Special Metals INCOLOY® Alloy 800 A nickel-iron-chromium alloy with good strength and excellent resistance to oxidation and carburization in high-temperature atmospheres. It also resists corrosion by many aqueous environments. The.. |
|||
Tensile Strength, Ultimate | <= 500 MPa | <= 72500 psi | |
SSAB Tunnplat Aluzink B500A Metal-coated Mild Steel Metal-coated Mild SteelComments: Aluzink - Aluminum-zinc coated sheet. Property values are for thicknesses 0.4 - 2.00 mm. Iron content is approximate - exact composition is not reported by the manu.. |
|||
Tensile Strength, Ultimate | <= 500 MPa | <= 72500 psi | |
SSAB Tunnplat Dogal B500 Metal-coated Mild Steel Metal-coated Mild SteelComments: Dogal - Hotdipped-galvanized sheet. Property values are for thicknesses 0.5 - 2.5 mm. Iron content is approximate - exact composition is not reported by the manufac.. |
|||
Tensile Strength, Ultimate | 500 MPa | 72500 psi | |
Wieland 1401 Wilaform Gold Hard standard yellow gold alloy. Easily splintered and polished thus very well suited for crafts and industrial decoration manufacturing.Applications: casting, chains, laminar decoration, pipes, tu.. |
|||
Tensile Strength, Ultimate | 500 MPa | 72500 psi | |
Wieland 1602 Wilaform Gold Hard standard yellow gold alloy. Easily splintered and polished thus very well suited for crafts and industrial decoration manufacturing.Applications: casting, chains, laminar decoration, pipes, tu.. |
|||
Tensile Strength, Ultimate | 500 - 550 MPa | 72500 - 79800 psi | Rod |
CLAL-MSX ARCAP Anticorrosion AP1 H13 3/4 hard, Drawn Copper Alloy Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (accordin.. |
|||
Tensile Strength, Ultimate | 500 - 580 MPa | 72500 - 84100 psi | |
CLAL-MSX NICLAFOR® 1000 TD1 Quenched/Cold Rolled, Drawn Copper Alloy Finished parts can be produced with: reduction in sections, high mechanical properties even at high temperature, high spring properties, high conductivity, good resistance to corrosion, low permeabi.. |
|||
Tensile Strength, Ultimate | 500 - 550 MPa | 72500 - 79800 psi | Rod |
CLAL-MSX ARCAP Anticorrosion AP1C H12 1/2 hard, Drawn Copper Alloy Description: The AP1C grade (used in rods for parts that are to be deformed by torsion, bending, riveting, swaging... and for welding) and the AP1 grade (sheet, strip, wire, tubes) is machineable un.. |
|||
Tensile Strength, Ultimate | 500 - 550 MPa | 72500 - 79800 psi | Rod |
CLAL-MSX ARCAP Anticorrosion AP4 H11 1/4 hard, Drawn Copper Alloy Description: The AP4 grade is less easy to turn than the other grades of ARCAP. It can however be machined without more difficulty than the nickel chromium molybdenum steels.High Corrosion Resistanc.. |
|||
Tensile Strength, Ultimate | 500 MPa | 72500 psi | As Cast |
AFE Technologies Cronite 25Cr/20Ni No. HR6 High temperature nickel alloy castings. Applications include heat treatment and handling products, furnace products, tubes, power generation, and petrochemical industries.Information provided by AF.. |
|||
Tensile Strength, Ultimate | 500 MPa | 72500 psi | |
ATI Allegheny Ludlum AL 304DA Stainless/Carbon Steel Three-Ply Composite Composition above represents only the Type 304 cladding. Its iron content calculated as balance.Allegheny Ludlum AL 304DA is tri-ply composite consisting of a dual stabilized, low carbon steel cent.. |
|||
Tensile Strength, Ultimate | 500 - 700 MPa | 72500 - 102000 psi | before hot stamping |
ArcelorMittal Usibor® 1500 Ultra high strength steel, Cold Rolled Description: Usibor® 1500 and 22MnB5 are hot formed grades intended for use in automobile structural and safety components. The very high mechanical strength of the final part makes it possible to .. |
|||
Tensile Strength, Ultimate | 500 - 700 MPa | 72500 - 102000 psi | before hot stamping |
ArcelorMittal Usibor® 1500 Ultra high strength steel, Hot Rolled Description: Usibor® 1500 and 22MnB5 are hot formed grades intended for use in automobile structural and safety components. The very high mechanical strength of the final part makes it possible to .. |
|||
Tensile Strength, Ultimate | 500 - 700 MPa | 72500 - 102000 psi | before hot stamping |
ArcelorMittal Usibor® 22MnB5 Ultra high strength steel, Cold Rolled Description: Usibor® 1500 and 22MnB5 are hot formed grades intended for use in automobile structural and safety components. The very high mechanical strength of the final part makes it possible to .. |
|||
Tensile Strength, Ultimate | 500 - 700 MPa | 72500 - 102000 psi | before hot stamping |
ArcelorMittal Usibor® 22MnB5 Ultra high strength steel, Hot Rolled Description: Usibor® 1500 and 22MnB5 are hot formed grades intended for use in automobile structural and safety components. The very high mechanical strength of the final part makes it possible to .. |
|||
Tensile Strength, Ultimate | 500 MPa | 72500 psi | As Cast |
AFE Technologies Cronite Standard Nickel Alloy Castings, No. HR4 High temperature nickel alloy castings. Applications include heat treatment and handling products, furnace products, tubes, power generation, and petrochemical industries.Information provided by AF.. |
|||
Tensile Strength, Ultimate | 500 MPa | 72500 psi | |
Haynes 556® alloy, bar after 16000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Tensile Strength, Ultimate | 500 MPa @Temperature 100 °C |
72500 psi @Temperature 212 °F |
EN min.; EN 10002-5 |
Outokumpu 904L High Performance Austenitic Stainless Steel Applications: Process equipment in chemical industryBleaching equipment in the pulp and paper industryFlue-gas cleaningDesalinationSeawater handlingHeat exchangersAvailable in hot rolled plate (Quar.. |