CLAL-MSX ARCAP Anticorrosion AP1 H13 3/4 hard, Drawn Copper Alloy

Category Metal , Nonferrous Metal , Copper Alloy
Manufacturer CLAL-MSX
Trade Name ARCAP Anticorrosion
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF CLAL-MSX ARCAP Anticorrosion AP1 H13 3/4 hard, Drawn Copper Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: The AP1D grade has been developed especially for being machined by lathe. The very good machineability of the AP1D grade may be summerised by: cutting speed up to 150 m/minute (according to the type of part, cutting tool and lathe), very good quality of surface that can be lapped or polished with a diamond tool, burr free after drilling, and reduction in frequency of tool sharpening.High Corrosion Resistance: ARCAP alloys are very corrosion resistant to the majority of chemical and physical environments. CLAL can provide data for the corrosion resistance of ARCAP alloys. In particular ARCAP alloys have a very high resistance to scaling and clogging of pipes by hard water and the blocking of pipes used for transport powder products such as sodium aluminate, cement, etc. High Mechanical Properties: In annealed temper ARCAP, alloys have an elongation up to 45 %, which allows deep drawing. In spring temper the ultimate tensile strength is above 800 MPa. Non-Magnetic: A detector sensitive to 1/10 of nanotesla, placed at less than 1 mm from ARCAP alloys will not show any magnetic interference. This non magnetism is kept even at very low temperatures (measured at 4.2° k). Stable Resistivity: Temperature variations have almost no effect on the resistivity of ARCAP alloys. The temperature coefficient of the grade AP4 is 4 x 10-5/°C and 25 x 10-5/°C for the other grades. Excellent Behaviour At Low Temperature: At low temperatures the mechanical properties of ARCAP alloys are improved. A cryogenic application shows that the ultimate tensile strength and the yield strength increase without any diminution of the elongation or the impact strength. Very Easy To Process: ARCAP alloys are easily processed whether by forging, stamping, deep drawing, machining, welding or brazing. They are also easily plated.Information provided by CLAL-MSX
Physical Properties Metric English Comments
Density 8.80 g/cc
0.318 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 500 - 550 MPa
72500 - 79800 psi
Rod
550 - 610 MPa
79800 - 88500 psi
Wire
Elongation at Break >= 2.0 %
>= 2.0 %
L<sub>O</sub>=50 mm
Modulus of Elasticity 163 - 170 GPa
23600 - 24700 ksi
Thermal Properties Metric English Comments
CTE, linear 16.0 µm/m-°C

@Temperature 0.000 - 300 °C
8.89 µin/in-°F

@Temperature 32.0 - 572 °F
17.0 µm/m-°C

@Temperature 0.000 - 600 °C
9.44 µin/in-°F

@Temperature 32.0 - 1110 °F
Thermal Conductivity 22.0 W/m-K

@Temperature <=20.0 °C
153 BTU-in/hr-ft²-°F

@Temperature <=68.0 °F
25.0 W/m-K

@Temperature <=200 °C
174 BTU-in/hr-ft²-°F

@Temperature <=392 °F
Melting Point 1150 - 1170 °C
2100 - 2140 °F
Solidus 1150 °C
2100 °F
Liquidus 1170 °C
2140 °F
Optical Properties Metric English Comments
Reflection Coefficient, Visible (0-1) 0.700
0.700
Relative to Silver = 1
Component Elements Properties Metric English Comments
Copper, Cu 65 %
65 %
Nickel, Ni 25 %
25 %
Other 2.0 %
2.0 %
Zinc, Zn 8.0 %
8.0 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000351 - 0.0000400 ohm-cm
0.0000351 - 0.0000400 ohm-cm
Descriptive Properties Value Comments
Color Whiteish bluish
Non Magnetism request 1E-05
OERSTED
Temperature Coefficient 0.00025
K-1