AFE Technologies Cronite 25Cr/20Ni No. HR6

Category	Metal , Superalloy , Iron Base
Manufacturer	AFE TEchnologies; North American Cronite
Trade Name	Cronite
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	AFE Technologies Cronite 25Cr/20Ni No. HR6.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

High temperature nickel alloy castings. Applications include heat treatment and handling products, furnace products, tubes, power generation, and petrochemical industries.Information provided by AFE Technologies/North American Cronite, Inc.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	500 MPa	72500 psi	As Cast
Tensile Strength, Yield	260 MPa	37700 psi	As Cast
Elongation at Break	12 %	12 %	As Cast; 5.65 A<sup>0.5</sup>
Rupture Strength	2.20 MPa @Temperature 1150 °C, Time 3.60e+7 sec	319 psi @Temperature 2100 °F, Time 10000 hour	Stress Rupture
	3.80 MPa @Temperature 1100 °C, Time 3.60e+7 sec	551 psi @Temperature 2010 °F, Time 10000 hour	Stress Rupture
	6.00 MPa @Temperature 1050 °C, Time 3.60e+7 sec	870 psi @Temperature 1920 °F, Time 10000 hour	Stress Rupture
	9.50 MPa @Temperature 1000 °C, Time 3.60e+7 sec	1380 psi @Temperature 1830 °F, Time 10000 hour	Stress Rupture
	14.5 MPa @Temperature 950 °C, Time 3.60e+7 sec	2100 psi @Temperature 1740 °F, Time 10000 hour	Stress Rupture
	21.0 MPa @Temperature 900 °C, Time 3.60e+7 sec	3050 psi @Temperature 1650 °F, Time 10000 hour	Stress Rupture
	30.0 MPa @Temperature 850 °C, Time 3.60e+7 sec	4350 psi @Temperature 1560 °F, Time 10000 hour	Stress Rupture
	41.0 MPa @Temperature 800 °C, Time 3.60e+7 sec	5950 psi @Temperature 1470 °F, Time 10000 hour	Stress Rupture
	55.0 MPa @Temperature 750 °C, Time 3.60e+7 sec	7980 psi @Temperature 1380 °F, Time 10000 hour	Stress Rupture
	72.0 MPa @Temperature 700 °C, Time 3.60e+7 sec	10400 psi @Temperature 1290 °F, Time 10000 hour	Stress Rupture

Component Elements Properties	Metric	English	Comments
Carbon, C	0.40 %	0.40 %
Chromium, Cr	25 %	25 %
Iron, Fe	52.1 %	52.1 %	As Remainder
Manganese, Mn	1.0 %	1.0 %
Nickel, Ni	20 %	20 %
Silicon, Si	1.5 %	1.5 %

Users viewing this material also viewed the following: