Outokumpu 904L High Performance Austenitic Stainless Steel

Category Metal , Ferrous Metal , Austenitic , Pressure Vessel Steel , Stainless Steel
Manufacturer Outokumpu
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Outokumpu 904L High Performance Austenitic Stainless Steel.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Applications: Process equipment in chemical industryBleaching equipment in the pulp and paper industryFlue-gas cleaningDesalinationSeawater handlingHeat exchangersAvailable in hot rolled plate (Quarto), hot rolled strip/sheet (CPP), cold rolled strip/sheet, cold rolled narrow strip, bar, and rod forms.
Physical Properties Metric English Comments
Density 8.00 g/cc
0.289 lb/in³
RT
Mechanical Properties Metric English Comments
Hardness, Brinell >= 180
>= 180
Hot rolled plate/Hot rolled strip/Cold rolled strip; EN 10003-1
Tensile Strength, Ultimate 600 MPa
87000 psi
Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
440 MPa

@Temperature 300 °C
 63800 psi

@Temperature 572 °F
 EN min.; EN 10002-5
460 MPa

@Temperature 200 °C
 66700 psi

@Temperature 392 °F
 EN min.; EN 10002-5
500 MPa

@Temperature 100 °C
 72500 psi

@Temperature 212 °F
 EN min.; EN 10002-5
Tensile Strength, Yield 220 MPa

@Strain 0.200 %
 31900 psi

@Strain 0.200 %
 EN min.,RT; EN 10002-1
260 MPa

@Strain 0.200 %
 37700 psi

@Strain 0.200 %
 Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1
300 MPa

@Strain 1.00 %
 43500 psi

@Strain 1.00 %
 Outokumpu Typical,Hot Rolled Plate (Quarto); EN 10002-1
125 MPa

@Strain 0.200 %,
Temperature 400 °C
 18100 psi

@Strain 0.200 %,
Temperature 752 °F
 EN min.; EN 10002-5
145 MPa

@Strain 0.200 %,
Temperature 300 °C
 21000 psi

@Strain 0.200 %,
Temperature 572 °F
 EN min.; EN 10002-5
155 MPa

@Strain 1.00 %,
Temperature 400 °C
 22500 psi

@Strain 1.00 %,
Temperature 752 °F
 EN min.; EN 10002-5
175 MPa

@Strain 1.00 %,
Temperature 300 °C
 25400 psi

@Strain 1.00 %,
Temperature 572 °F
 EN min.; EN 10002-5
175 MPa

@Strain 0.200 %,
Temperature 200 °C
 25400 psi

@Strain 0.200 %,
Temperature 392 °F
 EN min.; EN 10002-5
205 MPa

@Strain 0.200 %,
Temperature 100 °C
 29700 psi

@Strain 0.200 %,
Temperature 212 °F
 EN min.; EN 10002-5
205 MPa

@Strain 1.00 %,
Temperature 200 °C
 29700 psi

@Strain 1.00 %,
Temperature 392 °F
 EN min.; EN 10002-5
235 MPa

@Strain 1.00 %,
Temperature 100 °C
 34100 psi

@Strain 1.00 %,
Temperature 212 °F
 EN min.; EN 10002-5
Elongation at Break 50 %
50 %
Outokumpu Typical, Hot Rolled Plate (Quarto); EN 10002-1
Modulus of Elasticity 195 GPa
28300 ksi
RT
166 GPa

@Temperature 400 °C
 24100 ksi

@Temperature 752 °F
Poissons Ratio 0.30
0.30
RT
Shear Modulus 75.0 GPa
10900 ksi
calculated
Impact Test >= 60.0 J
>= 44.3 ft-lb
Hot rolled plate/Hot rolled strip/Cold rolled strip; EN 10045-1
Thermal Properties Metric English Comments
CTE, linear 15.8 µm/m-°C

@Temperature 100 °C
 8.78 µin/in-°F

@Temperature 212 °F
16.9 µm/m-°C

@Temperature 400 °C
 9.39 µin/in-°F

@Temperature 752 °F
Specific Heat Capacity 0.450 J/g-°C
0.108 BTU/lb-°F
RT
Thermal Conductivity 12.0 W/m-K
83.3 BTU-in/hr-ft²-°F
RT
18.0 W/m-K

@Temperature 400 °C
 125 BTU-in/hr-ft²-°F

@Temperature 752 °F
Component Elements Properties Metric English Comments
Carbon, C 0.010 %
0.010 %
Chromium, Cr 20 %
20 %
Copper, Cu 1.5 %
1.5 %
Iron, Fe 49.19 %
49.19 %
Molybdenum, Mo 4.3 %
4.3 %
Nickel, Ni 25 %
25 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.000100 ohm-cm
0.000100 ohm-cm
RT
Processing Properties Metric English Comments
Annealing Temperature 1080 - 1160 °C
1980 - 2120 °F
Solution Annealing