Polymer Property : Tensile Strength, Ultimate = 200 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	40.0 - 200 MPa @Temperature -40.0 - 140 °C	5800 - 29000 psi @Temperature -40.0 - 284 °F	Average value: 93.9 MPa Grade Count:1
Overview of materials for Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled". Specific grades with glass content between 25..
Tensile Strength, Ultimate	40.0 - 200 MPa @Strain 0.500 - 5.00 %	5800 - 29000 psi @Strain 0.500 - 5.00 %	Average value: 93.9 MPa Grade Count:1
Overview of materials for Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled". Specific grades with glass content between 25..
Tensile Strength, Ultimate	9.25 - 200 MPa	1340 - 29000 psi	Average value: 101 MPa Grade Count:35
Overview of materials for Polyphthalamide (PPA), 20% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 20% Glass Fiber Reinforced". Specific grades with glass content between 15% and 24% are..
Tensile Strength, Ultimate	131 - 200 MPa	19000 - 29000 psi	Average value: 170 MPa Grade Count:5
Overview of materials for Polyetherketoneetherketoneketone (PEKEKK), Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyetherketoneetherketoneketone (PEKEKK), Glass Fiber Filled". Each property range of values reported i..
Tensile Strength, Ultimate	177 - 200 MPa	25600 - 29000 psi	Average value: 187 MPa Grade Count:5
Overview of materials for Polyetherimide (PEI), 40% Glass Fiber This property data is a summary of similar materials in the MatWeb database for the category "Polyetherimide, 40% Glass Fiber". Specific grades with glass content between 35% and 44% are included. E..
Tensile Strength, Ultimate	100 - 200 MPa	14500 - 29000 psi	Average value: 162 MPa Grade Count:12
Overview of materials for Liquid Crystal Polymer (LCP), 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), 20% Glass Fiber Filled". Specific grades with glass content between 15% an..
Tensile Strength, Ultimate	102 - 200 MPa	14800 - 29000 psi	Average value: 148 MPa Grade Count:17
Overview of materials for Liquid Crystal Polymer (LCP), Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), Carbon Fiber Filled". Each property range of values reported is minimum an..
Tensile Strength, Ultimate	48.0 - 200 MPa @Temperature -40.0 - 150 °C	6960 - 29000 psi @Temperature -40.0 - 302 °F	Average value: 86.6 MPa Grade Count:1
Overview of materials for Liquid Crystal Polymer (LCP), Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), Mineral Filled". Each property range of values reported is minimum and max..
Tensile Strength, Ultimate	36.5 - 200 MPa	5300 - 29000 psi	Average value: 147 MPa Grade Count:17
Overview of materials for Polyphenylene Sulfide (PPS) with 50% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 50% Glass Fiber Filler". Specific grades with glass content between 45%..
Tensile Strength, Ultimate	50.0 - 200 MPa	7250 - 29000 psi	Average value: 132 MPa Grade Count:127
Overview of materials for Nylon 66, Glass Fiber Filled, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass Fiber Filled, Flame Retardant". Each property range of values reported is minimum and ma..
Tensile Strength, Ultimate	44.8 - 200 MPa	6500 - 29000 psi	Average value: 131 MPa Grade Count:141
Overview of materials for Nylon 612, Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Nylon 612, Glass Fiber Filler". Each property range of values reported is minimum and maximum values of ..
Tensile Strength, Ultimate	100 - 200 MPa	14500 - 29000 psi	Average value: 150 MPa Grade Count:17
Overview of materials for Nylon 46, Flame Retarded + Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Flame Retarded + Glass Fiber Reinforced". Each property range of values reported is minimum an..
Tensile Strength, Ultimate	22.4 - 200 MPa @Temperature -40.0 - 150 °C	3250 - 29000 psi @Temperature -40.0 - 302 °F	Average value: 87.1 MPa Grade Count:1
Overview of materials for Polyethylene Terephthalate (PET), 40% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), 40% Glass Reinforced". Specific grades with glass content between 35% ..
Tensile Strength, Ultimate	22.4 - 200 MPa @Strain 0.140 - 4.69 %	3250 - 29000 psi @Strain 0.140 - 4.69 %	Average value: 87.1 MPa Grade Count:1
Overview of materials for Polyethylene Terephthalate (PET), 40% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), 40% Glass Reinforced". Specific grades with glass content between 35% ..
Tensile Strength, Ultimate	22.0 - 200 MPa	3190 - 29000 psi	Average value: 62.0 MPa Grade Count:104
Overview of materials for Nylon 6, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Impact Grade". Each property range of values reported is minimum and maximum values of appropri..