Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 12.5 - 110 MPa | 1810 - 16000 psi | Average value: 75.0 MPa Grade Count:65 |
Overview of materials for Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled".Specific grades with glass content between 5% .. |
|||
Tensile Strength, Ultimate | 44.8 - 110 MPa | 6500 - 16000 psi | Average value: 74.2 MPa Grade Count:32 |
Overview of materials for Acetal Copolymer, 10% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, 10% Glass Fiber Reinforced". Specific grades with glass content between 5% and 14% ar.. |
|||
Tensile Strength, Ultimate | 38.0 - 110 MPa | 5510 - 16000 psi | Average value: 54.5 MPa Grade Count:12 |
Overview of materials for Acetal Copolymer, Silicone Filled This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, Silicone Filled". Each property range of values reported is minimum and maximum values.. |
|||
Tensile Strength, Ultimate | 16.0 - 110 MPa | 2320 - 16000 psi | Average value: 67.9 MPa Grade Count:16 |
Overview of materials for Polycarbonate, Conductive This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Conductive". Each property range of values reported is minimum and maximum values of appr.. |
|||
Tensile Strength, Ultimate | 35.0 - 110 MPa | 5080 - 16000 psi | Average value: 55.1 MPa Grade Count:85 |
Overview of materials for Polycarbonate/PET Polyester Blend This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/PET Polyester Blend". Each property range of values reported is minimum and maximum values.. |
|||
Tensile Strength, Ultimate | 30.0 - 110 MPa | 4350 - 16000 psi | Average value: 49.7 MPa Grade Count:131 |
Overview of materials for Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced". Each property range of values repor.. |
|||
Tensile Strength, Ultimate | 110 - 110 MPa @Temperature >=130 °C |
16000 - 16000 psi @Temperature >=266 °F |
Average value: 128 MPa Grade Count:1 |
Overview of materials for Nylon 66/6, 40% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 40% Glass Fiber Reinforced". Specific grades with glass content between 35% and 44% are incl.. |
|||
Tensile Strength, Ultimate | 110 - 110 MPa @Time 1.80e+7 - 7.20e+7 sec |
16000 - 16000 psi @Time 5000 - 20000 hour |
Average value: 128 MPa Grade Count:1 |
Overview of materials for Nylon 66/6, 40% Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 40% Glass Fiber Reinforced". Specific grades with glass content between 35% and 44% are incl.. |
|||
Tensile Strength, Ultimate | 49.6 - 110 MPa | 7200 - 16000 psi | Average value: 71.1 MPa Grade Count:12 |
Overview of materials for Nylon 66, Mineral Filled, Impact Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Mineral Filled, Impact Grade". Each property range of values reported is minimum and maximum v.. |
|||
Tensile Strength, Ultimate | 68.9 - 110 MPa | 10000 - 16000 psi | Average value: 81.7 MPa Grade Count:12 |
Overview of materials for Nylon 11 with 20% Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Nylon 11 with 20% Glass Fiber Filler". Specific grades with glass content between 15% and 24% are includ.. |
|||
Tensile Strength, Ultimate | 15.0 - 110 MPa @Temperature 60.0 - 150 °C |
2180 - 16000 psi @Temperature 140 - 302 °F |
Average value: 58.4 MPa Grade Count:4 |
Overview of materials for Nylon 12 This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12". Each property range of values reported is minimum and maximum values of appropriate MatWeb en.. |
|||
Tensile Strength, Ultimate | 38.0 - 110 MPa | 5510 - 16000 psi | Average value: 88.2 MPa Grade Count:25 |
Overview of materials for Nylon 12, 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 20% Glass Fiber Filled". Specific grades with glass content between 15% and 24% are included. .. |
|||
Tensile Strength, Ultimate | 55.0 - 110 MPa @Temperature 60.0 - 150 °C |
7980 - 16000 psi @Temperature 140 - 302 °F |
Average value: 83.8 MPa Grade Count:1 |
Overview of materials for Nylon 12, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 12, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. .. |
|||
Tensile Strength, Ultimate | 90.0 - 110 MPa | 13100 - 16000 psi | ASTM D638 |
Chang Chun Plastic PBT4815 Fire Retardant & 15% Glass Fiber Enforced Grade PBT Information provided by Dowell Trading Company Ltd. |
|||
Tensile Strength, Ultimate | 90.0 - 110 MPa | 13100 - 16000 psi | ASTM D638 |
Chang Chun Plastic PBT4115 Fire Retardant & 15% Glass Fiber Enforced Grade PBT Information provided by Dowell Trading Company Ltd. |
|||
Tensile Strength, Ultimate | 90.0 - 110 MPa @Temperature 120 - 160 °C |
13100 - 16000 psi @Temperature 248 - 320 °F |
Average value: 100 MPa Grade Count:1 |
Overview of materials for Nylon 46, Flame Retarded + Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 46, Flame Retarded + Glass Fiber Reinforced". Each property range of values reported is minimum an.. |
|||
Tensile Strength, Ultimate | 90.0 - 110 MPa | 13100 - 16000 psi | Average value: 103 MPa Grade Count:3 |
Overview of materials for PEKK, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "PEKK, Unreinforced". Each property range of values reported is minimum and maximum values of appropriate.. |
|||
Tensile Strength, Ultimate | 40.0 - 110 MPa | 5800 - 16000 psi | Average value: 84.1 MPa Grade Count:38 |
Overview of materials for Acetal Copolymer + Glass/PTFE This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer + Glass/PTFE". Each property range of values reported is minimum and maximum values of .. |
|||
Tensile Strength, Ultimate | 80.0 - 110 MPa @Temperature 60.0 - 150 °C |
11600 - 16000 psi @Temperature 140 - 302 °F |
Average value: 95.0 MPa Grade Count:1 |
Overview of materials for Polyethersulfone (PES), 20% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone (PES), 20% Glass Fiber Filled". Each property range of values reported is minimum and m.. |
|||
Tensile Strength, Ultimate | 75.0 - 110 MPa | 10900 - 16000 psi | Average value: 88.0 MPa Grade Count:5 |
Overview of materials for Polyphenylene Ether + Styrene-Butadiene Blend, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Ether + Styrene-Butadiene Blend, Glass Filled". Each property range of values reported is .. |
|||
Tensile Strength, Ultimate | 40.0 - 110 MPa @Temperature -40.0 - 70.0 °C |
5800 - 16000 psi @Temperature -40.0 - 158 °F |
Average value: 75.0 MPa Grade Count:3 |
Overview of materials for Acrylic, Cast This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Cast". Each property range of values reported is minimum and maximum values of appropriate MatW.. |
|||
Tensile Strength, Ultimate | 20.0 - 110 MPa | 2900 - 16000 psi | Average value: 67.7 MPa Grade Count:184 |
Overview of materials for Nylon 6, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Unreinforced". Each property range of values reported is minimum and maximum values of appropri.. |
|||
Tensile Strength, Ultimate | 45.0 - 110 MPa @Temperature 60.0 - 150 °C |
6530 - 16000 psi @Temperature 140 - 302 °F |
Average value: 73.8 MPa Grade Count:1 |
Overview of materials for Polybutylene Terephthalate (PBT), Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Carbon Fiber Filled". Each property range of values reported is minimu.. |