Overview of materials for Liquid Crystal Polymer (LCP), Mineral Filled

Category Polymer , Thermoplastic , Liquid Crystal Polymer (LCP) , Liquid Crystal Polymer (LCP), Mineral Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Liquid Crystal Polymer (LCP), Mineral Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), Mineral Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.52 - 1.89 g/cc
0.0549 - 0.0683 lb/in³
Average value: 1.69 g/cc Grade Count:24
Filler Content 30.0 - 50.0 %
30.0 - 50.0 %
Average value: 38.0 % Grade Count:5
Water Absorption 0.0200 - 0.100 %
0.0200 - 0.100 %
Average value: 0.0425 % Grade Count:8
Moisture Absorption at Equilibrium 0.0200 - 0.0400 %
0.0200 - 0.0400 %
Average value: 0.0233 % Grade Count:6
Linear Mold Shrinkage 0.000 - 0.00300 cm/cm
0.000 - 0.00300 in/in
Average value: 0.00100 cm/cm Grade Count:19
Linear Mold Shrinkage, Transverse 0.00200 - 0.0110 cm/cm
0.00200 - 0.0110 in/in
Average value: 0.00545 cm/cm Grade Count:17
Mechanical Properties Metric English Comments
Hardness, Rockwell M 43.0 - 79.0
43.0 - 79.0
Average value: 62.0 Grade Count:7
Tensile Strength, Ultimate 76.0 - 175 MPa
11000 - 25400 psi
Average value: 132 MPa Grade Count:24
48.0 - 200 MPa

@Temperature -40.0 - 150 °C
6960 - 29000 psi

@Temperature -40.0 - 302 °F
Average value: 86.6 MPa Grade Count:1
17.0 - 216 MPa

@Temperature -40.0 - 250 °C
2470 - 31300 psi

@Temperature -40.0 - 482 °F
Average value: 86.6 MPa Grade Count:1
17.0 - 216 MPa

@Thickness 1.60 - 3.17 mm
2470 - 31300 psi

@Thickness 0.0630 - 0.125 in
Average value: 86.6 MPa Grade Count:1
Elongation at Break 1.20 - 5.50 %
1.20 - 5.50 %
Average value: 3.44 % Grade Count:22
2.50 - 3.20 %

@Temperature 120 - 150 °C
2.50 - 3.20 %

@Temperature 248 - 302 °F
Average value: 2.06 % Grade Count:1
0.700 - 3.20 %

@Temperature -40.0 - 250 °C
0.700 - 3.20 %

@Temperature -40.0 - 482 °F
Average value: 2.06 % Grade Count:1
0.700 - 3.20 %

@Thickness 1.60 - 3.17 mm
0.700 - 3.20 %

@Thickness 0.0630 - 0.125 in
Average value: 2.06 % Grade Count:1
Modulus of Elasticity 8.50 - 22.0 GPa
1230 - 3190 ksi
Average value: 12.6 GPa Grade Count:21
4.80 - 11.6 GPa

@Temperature -40.0 - 150 °C
696 - 1680 ksi

@Temperature -40.0 - 302 °F
Average value: 7.45 GPa Grade Count:1
2.77 - 16.5 GPa

@Temperature -40.0 - 250 °C
402 - 2390 ksi

@Temperature -40.0 - 482 °F
Average value: 7.45 GPa Grade Count:1
2.77 - 16.5 GPa

@Thickness 1.60 - 3.17 mm
402 - 2390 ksi

@Thickness 0.0630 - 0.125 in
Average value: 7.45 GPa Grade Count:1
Flexural Yield Strength 110 - 220 MPa
16000 - 31900 psi
Average value: 155 MPa Grade Count:21
42.0 - 260 MPa

@Temperature -40.0 - 150 °C
6090 - 37700 psi

@Temperature -40.0 - 302 °F
Average value: 109 MPa Grade Count:2
42.0 - 260 MPa

@Thickness 0.800 - 3.17 mm
6090 - 37700 psi

@Thickness 0.0315 - 0.125 in
Average value: 109 MPa Grade Count:2
Flexural Modulus 6.60 - 20.0 GPa
957 - 2900 ksi
Average value: 11.5 GPa Grade Count:24
3.30 - 16.7 GPa

@Temperature -40.0 - 150 °C
479 - 2420 ksi

@Temperature -40.0 - 302 °F
Average value: 7.38 GPa Grade Count:2
3.30 - 16.7 GPa

@Thickness 0.800 - 3.17 mm
479 - 2420 ksi

@Thickness 0.0315 - 0.125 in
Average value: 7.38 GPa Grade Count:2
Compressive Yield Strength 51.7 - 131 MPa
7500 - 19000 psi
Average value: 81.6 MPa Grade Count:8
Compressive Modulus 9.50 - 21.5 GPa
1380 - 3120 ksi
Average value: 14.1 GPa Grade Count:7
Izod Impact, Notched 0.587 - 1.60 J/cm
1.10 - 3.00 ft-lb/in
Average value: 1.12 J/cm Grade Count:4
Izod Impact, Notched (ISO) 5.00 - 60.0 kJ/m²
2.38 - 28.6 ft-lb/in²
Average value: 26.9 kJ/m² Grade Count:12
Charpy Impact Unnotched 5.00 - 8.40 J/cm²
23.8 - 40.0 ft-lb/in²
Average value: 6.76 J/cm² Grade Count:5
4.00 - 4.00 J/cm²

@Temperature -30.0 - -30.0 °C
19.0 - 19.0 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 4.00 J/cm² Grade Count:2
Charpy Impact, Notched 0.360 - 4.00 J/cm²
1.71 - 19.0 ft-lb/in²
Average value: 1.37 J/cm² Grade Count:17
0.700 - 0.800 J/cm²

@Temperature -30.0 - -30.0 °C
3.33 - 3.81 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 0.750 J/cm² Grade Count:2
Tensile Impact Strength 40.0 - 80.0 kJ/m²
19.0 - 38.1 ft-lb/in²
Average value: 56.7 kJ/m² Grade Count:3
Coefficient of Friction 0.120 - 0.210
0.120 - 0.210
Average value: 0.172 Grade Count:4
Thermal Properties Metric English Comments
CTE, linear -10.0 - 15.0 µm/m-°C
-5.56 - 8.33 µin/in-°F
Average value: 5.52 µm/m-°C Grade Count:15
-4.00 - 20.0 µm/m-°C

@Temperature 55.0 - 260 °C
-2.22 - 11.1 µin/in-°F

@Temperature 131 - 500 °F
Average value: 8.00 µm/m-°C Grade Count:3
-4.00 - 20.0 µm/m-°C

@Thickness 2.00 - 4.00 mm
-2.22 - 11.1 µin/in-°F

@Thickness 0.0787 - 0.157 in
Average value: 8.00 µm/m-°C Grade Count:3
CTE, linear, Transverse to Flow 22.0 - 69.0 µm/m-°C
12.2 - 38.3 µin/in-°F
Average value: 43.8 µm/m-°C Grade Count:15
34.0 - 62.0 µm/m-°C

@Temperature 55.0 - 260 °C
18.9 - 34.4 µin/in-°F

@Temperature 131 - 500 °F
Average value: 47.7 µm/m-°C Grade Count:3
34.0 - 62.0 µm/m-°C

@Thickness 2.00 - 4.00 mm
18.9 - 34.4 µin/in-°F

@Thickness 0.0787 - 0.157 in
Average value: 47.7 µm/m-°C Grade Count:3
Melting Point 280 - 335 °C
536 - 635 °F
Average value: 314 °C Grade Count:20
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+12 - 1.00e+16 ohm-cm
1.00e+12 - 1.00e+16 ohm-cm
Average value: 2.63e+15 ohm-cm Grade Count:14
Surface Resistance 1.00e+15 - 1.00e+17 ohm
1.00e+15 - 1.00e+17 ohm
Average value: 1.73e+16 ohm Grade Count:14
Dielectric Constant 2.90 - 6.70
2.90 - 6.70
Average value: 3.77 Grade Count:15
4.00 - 4.20

@Temperature 120 - 250 °C
4.00 - 4.20

@Temperature 248 - 482 °F
Average value: 4.06 Grade Count:2
4.00 - 4.20

@Frequency 1.00e+9 - 1.00e+10 Hz
4.00 - 4.20

@Frequency 1.00e+9 - 1.00e+10 Hz
Average value: 4.06 Grade Count:2
Dielectric Strength 26.0 - 49.0 kV/mm
660 - 1240 kV/in
Average value: 37.2 kV/mm Grade Count:8
Dissipation Factor 0.00100 - 0.0340
0.00100 - 0.0340
Average value: 0.0130 Grade Count:15
0.00500 - 0.0290

@Temperature 120 - 250 °C
0.00500 - 0.0290

@Temperature 248 - 482 °F
Average value: 0.0149 Grade Count:2
0.00500 - 0.0290

@Frequency 1.00e+9 - 1.00e+10 Hz
0.00500 - 0.0290

@Frequency 1.00e+9 - 1.00e+10 Hz
Average value: 0.0149 Grade Count:2
Arc Resistance 145 - 183 sec
145 - 183 sec
Average value: 175 sec Grade Count:7
Comparative Tracking Index 175 - 250 V
175 - 250 V
Average value: 204 V Grade Count:15