Polymer Property : Tensile Strength, Ultimate = 8.00 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 8.00 - 165 MPa
1160 - 23900 psi
Average value: 50.5 MPa Grade Count:86
Overview of materials for Polybutylene Terephthalate (PBT), Unreinforced, Molded
This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Unreinforced, Molded". Each property range of values reported is minim..
Tensile Strength, Ultimate 8.00 MPa
1160 psi
ASTM D638
ExxonMobil Optema® TC-221 Ethylene Methyl Acrylate for Compounding  (discontinued **)
Data provided by the manufacturer, Exxon Chemical.27% Methyl Acrylate. An Ethylene Methyl Acrylate copolymer which can be used for making alloys, blends, and compounds, or be injection molded where..
Tensile Strength, Ultimate 8.00 MPa
1160 psi
500 mm/min (20 in./min.); ASTM D638, Type IV Specimen
Eastman 18BOA Polyethylene  (discontinued **)
Polyethylene 18BOA is a low density formulation used for injection molding. It is an outstanding material for molding lids and other container closures because it processes easily on automatic mold..
Tensile Strength, Ultimate 8.00 MPa
1160 psi
500 mm/min (20 in./min.); Type IV Specimen; ASTM D638
Eastman 18DOA Polyethylene  (discontinued **)
Polyethylene 18DOA is a low density formulation suggested for the production of closures where a high melt index material is needed to meet shrinkage requirements and fast molding cycles. It molds ..
Tensile Strength, Ultimate 8.00 MPa
1160 psi
500 mm/min (20 in./min.); Type IV Specimen; ASTM D638
Eastman Voridian D4009-A Polyethylene  (discontinued **)
Voridian polyethylene D4009-A is a low density formulation used for injection molding. It is an outstanding material for molding lids and other container closures because it processes easily on aut..
Tensile Strength, Ultimate 8.00 MPa
1160 psi
500 mm/min (20 in./min.); ASTM D638, Type IV Specimen
Eastman D4044A Polyethylene  (discontinued **)
D4044-A is a low density formulation used for injection molding. It is an outstanding material for molding lids and other container closures because it processes easily on automatic molding equipme..
Tensile Strength, Ultimate 8.00 MPa
1160 psi
500 mm/min (20 in./min.); ASTM D638, Type IV Specimen
Eastman Voridian D4053-A Polyethylene  (discontinued **)
Voridian polyethylene D4053-A is a low density formulation used for injection molding. It is an outstanding material for molding lids and other container closures because it processes easily on aut..
Tensile Strength, Ultimate 8.00 MPa
1160 psi
500 mm/min (20 in./min.); ASTM D638, Type IV Specimen
Eastman Voridian E6838-010A Polyethylene  (discontinued **)
Voridian polyethylene E6838-010A is a low density formulation with medium slip used for injection molding. It is an outstanding material for molding lids and other container closures because it pro..
Tensile Strength, Ultimate 8.00 - 15.0 MPa

@Temperature 60.0 - 90.0 °C
1160 - 2180 psi

@Temperature 140 - 194 °F
Average value: 11.5 MPa Grade Count:1
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant". Each property range of values rep..
Tensile Strength, Ultimate 8.00 - 60.0 MPa

@Temperature 60.0 - 90.0 °C
1160 - 8700 psi

@Temperature 140 - 194 °F
Average value: 29.6 MPa Grade Count:3
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled". Specific grades with glass content betwe..
Tensile Strength, Ultimate 8.00 MPa
1160 psi
500 mm/min (20 in./min.); ASTM D638, Type IV Specimen
Eastman M3018-P Polyethylene  (discontinued **)
Low density polyethylene M3018-P is a specialty formulation suggested for low temperature extrusion coating applications. M3018-P has been found to exhibit good coatability and adhesion to various ..
Tensile Strength, Ultimate 8.00 - 39.0 MPa
1160 - 5660 psi
Average value: 17.0 MPa Grade Count:18
Overview of materials for Polytetrafluoroethylene (PTFE), Conductive Carbon Filled
This property data is a summary of similar materials in the MatWeb database for the category "Polytetrafluoroethylene (PTFE), Conductive Carbon Filled". Each property range of values reported is min..
Tensile Strength, Ultimate 8.00 MPa
1160 psi
ISO R527-1
LyondellBasell Hifaxâ„¢ CA45 Thermoplastic Olefin Resin
Key Features: medium melt flow, medium modulus thermoplastic elastomeric olefin resin, excellent balance of properties, excellent processability, good colorability, excellent surface appearanceAppli..
Tensile Strength, Ultimate 8.00 MPa
1160 psi
DIN 53504
Lubrizol ESTANE® T4065 Ester Based Thermoplastic Polyurethane (European Grade)
Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability ..
Tensile Strength, Ultimate 8.00 MPa
1160 psi
Dow Corning SILASTIC® 9220/55 KIT PARTS A&B
55 Durometer, 2-part, 1 to 1 mix, black Liquid Silicone Rubber.Information provided by Dow Corning
Tensile Strength, Ultimate 8.00 MPa
1160 psi
Dow Corning SILASTIC® Q7-4765 BIOMEDICAL GRADE ETR ELASTOMER, KIT
Two-part, platinum-catalyzed (1:1 by weight), enhanced tear-resistant silicone elastomers are heat cured high consistency silicone rubbers designed for use by customers fabricating medical devices.I..
Tensile Strength, Ultimate 8.00 MPa
1160 psi
Vulcanizate, Press cured, TC95 +3min at 160°C
Dow Nordel® IP 4725P Dense Extrusion
FormulationNordel® IP 4725P
Tensile Strength, Ultimate 8.00 - 24.0 MPa
1160 - 3480 psi
ATG s.r.l. HNBR Hydrogenated Nitrile Butadiene Rubber
Tensile Strength, Ultimate 8.00 - 23.0 MPa
1160 - 3340 psi
ATG s.r.l. XNBR Carboxylated Nitrile Rubber
Tensile Strength, Ultimate 8.00 MPa
1160 psi
cured 7 days @ 25°C
Abatron AboCast 8110-2/AboCure 8110-3 Flexible Epoxy
This epoxy system can achieve flexibility and plasticity without sacrificing adhesive, electrical, structural, and other properties. This compound is a clear (unfilled) basic formulation. Its applic..
Tensile Strength, Ultimate 8.00 MPa

@Temperature 250 °C
1160 psi

@Temperature 482 °F
ASTM D638
Asahi Glass Fluon® P-63P PFA Perfluoropolymer
Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character..
Tensile Strength, Ultimate 8.00 MPa

@Temperature 250 °C
1160 psi

@Temperature 482 °F
ASTM D638
Asahi Glass Fluon® P-810UP PFA Perfluoropolymer
Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character..
Tensile Strength, Ultimate 8.00 MPa
1160 psi
ASTM D638
Global S-1018 Low Density Polyethylene, Injection Molding Grade  (discontinued **)
Description-transparency, high toughness, flexibility, high impact strength, good chemical resistanceApplications-packagingMeets FDA requirements as listed in food additives regulation 21 CFR 117.15..
Tensile Strength, Ultimate 8.00 MPa
1160 psi
ASTM D638
Huntsman PE2050 Injection Molding Polyethylene  (discontinued **)
Homopolymer and FDA compliant.Features: High flow characteristics, good gloss, and processability.Applications: Injection molding: large moldings including housewares and toys.FDA Notes: Conforms to..
Tensile Strength, Ultimate 8.00 MPa
1160 psi
ASTM D638
Huntsman PE2080 Injection Molding Polyethylene  (discontinued **)
Homopolymer and FDA compliant.Features: Very high flow rapid set-up characteristics, excellent clarity, and gloss.Applications: Injection molding: lids and difficult to fill applications.FDA Notes: ..
Tensile Strength, Ultimate 8.00 - 9.00 MPa
1160 - 1310 psi
Average value: 8.50 MPa Grade Count:4
Overview of materials for Low Density Polyethylene (LDPE), Masterbatch Grade
This property data is a summary of similar materials in the MatWeb database for the category "Low Density Polyethylene (LDPE), Masterbatch Grade". Each property range of values reported is minimum a..
Tensile Strength, Ultimate 8.00 - 8.00 MPa

@Temperature 120 - 120 °C
1160 - 1160 psi

@Temperature 248 - 248 °F
Average value: 8.00 MPa Grade Count:1
Overview of materials for Cellulose Acetate Propionate, Molded
This property data is a summary of similar materials in the MatWeb database for the category "Cellulose Acetate Propionate, Molded". Each property range of values reported is minimum and maximum val..
Tensile Strength, Ultimate 8.00 - 13.0 MPa
1160 - 1890 psi
Average value: 10.2 MPa Grade Count:7
Overview of materials for Ethylene-Methyl Acrylate Copolymer, Compounding Grade
This property data is a summary of similar materials in the MatWeb database for the category "Ethylene-Methyl Acrylate Copolymer, Compounding Grade". Each property range of values reported is minimu..